牌号简介 About |
---|
KetaSpire® KT-880FP是一种高流动性等级的无增强聚醚醚酮(PEEK),以天然颜色细粉末形式提供,用于压缩成型和其他可以从细粉末形式中受益的用途。KetaSpire Peek是按照最高的行业标准生产的,具有独特的性能组合,包括优异的耐磨性、一流的抗疲劳性、易熔加工性、高纯度和对有机物、酸和碱的优异耐化学性。这些特性使其非常适合用于医疗、运输、电子、化学加工和其他工业用途。该树脂也可作为KetaSpire KT-880 NT以自然色颗粒形式提供注射成型。 KetaSpire® KT-880FP is the high-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural color fine powder form for compression molding and other uses that can benefit from the fine powder form. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing, and other industrial uses. The resin is also available as KetaSpire KT-880 NT in a natural-color pellet form for injection molding. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
53 | J/m | ASTM D256 |
-- -- |
4.9 | kJ/m² | ISO 180 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
无断裂 | ASTM D4812 , ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
160 | ℃ | ASTM D648 |
玻璃化转变温度 Glass transition temperature |
147 | ℃ | ASTM D3418 |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
DSC | ||
50℃ 50℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3 mm 3 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 4 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
-- -- 5 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield 6 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/1A/50 | |
断裂 fracture 6 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/1A/50 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,2.16kg 400℃,2.16kg |
g/10min | ASTM D1238 | |
收缩率 Shrinkage rate 3 |
ASTM D955 | ||
MD:0.318 mm MD:0.318 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 供应塑料粒子里加入润滑剂硬脂酸钙(0.01 % )的牌号,对于非润滑、本色牌号,订购KT-880 NL 。 |
2 一般属性:这些不能被视为规格。 |
3 5" x 0.5" x 0.125" |
4 0.039 in/min |
5 2.0 in/min |
【新闻资讯】查看全部
巴斯夫将索理思出售给铂金资本
2021-08-01 搜料网资讯: 近日,巴斯夫与克杜瑞公司(Clayton, DubilierRice)签署协议,将索理思出售给铂金资本(Platinum Equity)。该项交易意味着索理思的企业价值为52.5亿美元,其中包括约25亿美元的净债 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |