牌号简介 About |
---|
一种用于挤出中等密度泡沫的硬质PVC粉末混合物。 A rigid PVC powder compound for the extrusion of a medium density foam. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.748 to 0.848 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
饱和 saturated |
0.80 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
22℃ 22℃ |
1100 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
屈服,22℃ Yield, 22 ℃ |
17.9 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
|||
22℃ 22℃ |
1280 | MPa | ASTM D790 |
弯曲强度 bending strength |
|||
22℃ 22℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
22℃ 22℃ |
J/m | ASTM D256 | |
落下冲击阻力 Falling impact resistance 2 |
|||
22℃,Extruded at 370 to 380° F melt temperature 22℃,Extruded at 370 to 380° F melt temperature 2 |
J/cm | ASTM D4226 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:22℃ MD:22℃ |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
ASTM D635 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 程序 B |
【新闻资讯】查看全部
设计年产量为160万吨!壳牌位于宾夕法尼亚州的聚合物工厂开始运营
2022-11-29 扫描上图二维码,可以免费下载 搜料 APP 据全球能源新闻网11月18日报道,壳牌子公司壳牌化学阿巴拉契亚有限责任公司宣布,其宾夕法尼亚州化工项目Shell Polymers Monaca(SPM)已开始运营 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |