牌号简介 About |
---|
警告:此材料的状态为“商业:限量发行”。此材料的数据最近尚未验证。在指定此等级之前,请联系RTP公司以获取当前信息。玻璃纤维增强聚氨酯弹性体提供比基础树脂更大的尺寸稳定性。它们具有出色的冲击强度,并且仍然保持其弹性特性。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Glass fiber reinforced polyurethane elastomers offer greater dimensional stability than the base resin. They offer outstanding impact strength and still remain their elastomeric characteristics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.10 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.40 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
690 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3.2 mm 3.2 mm |
1400 | J/m | ASTM D4812 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
塑料净化严重,回收再利用非常紧急
2018-06-14 塑料可说是人类又爱又恨的朋友,带来方便的同时,也对地球造成难以挽回伤害,世界经济论坛(WEF)曾预测,假如再不落实塑料回收或减产,2050 年海洋塑料会比鱼还要多。 根据 Science Advances 研究,截至 2015 年,在美国共约 63 亿公吨塑料垃圾中,只有 9% 落实回收,剩下 12% 进焚化炉、约 79% 塑料最后归宿在垃圾掩埋场或随意丢弃。即使是拥有严格废弃物管理制度的欧洲国家,也只有 31% 塑料回收再利用,因此不少学者认为,如果无法好好回收塑料,那就 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |