牌号简介 About |
---|
材料类型:黑色氟橡胶化合物,硬度肖氏A 70-80。以双酚固化的三元共聚物为基础,其氟含量高于共聚物。特点:具有良好的流动性、抗热裂性、粘结性、对含醇燃料的耐腐蚀性。工艺方法:适用于压缩、转移、挤出、注塑等过程。用途:油封或其他需要金属粘合性能的零件,以及需要耐热撕裂的复杂几何形状。实验室测试固化条件:压力固化:10分钟@170°C。烘箱:(8+16)小时@230°C Material Type: Black color fluoroelastomer compound, hardness Shore A 70-80. Based on bisphenol curable terpolymer which is higher fluorine content than copolymer. Features: Excellent mold flow, hot tear resistance, bonding adhesion, good resistance to the fuel containing alcohols. Process Methods: Suitable for compression, transfer, extrusion and injection molding processes. Applications: Oil seals or other parts requiring metal bonding property, and complicated geometries requiring hot tear resistance. Lab Testing Curing Condition: Press Curing: 10min@170°C. Oven: (8+16)hrs@230°C |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.98 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
74 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
15.4 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
280 | % | ASTM D412 |
压缩形变 Compression deformation 2 |
|||
200℃,70 hr 200℃,70 hr 2 |
32 | % | ASTM D395 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
250℃,70 hr 250℃,70 hr |
% | ASTM D573 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
250℃,70 hr 250℃,70 hr |
% | ASTM D573 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
|||
250℃,70 hr 250℃,70 hr |
ASTM D573 | ||
拉伸强度的变化率 The rate of change in tensile strength |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
|||
23℃,70 hr,在基准燃料C中 23 ℃, 70 hr, in reference fuel C |
ASTM D471 | ||
体积变化 Volume change |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 6 mm Buttons |
【新闻资讯】查看全部
3D打印巨头公司Stratasys开发新型热塑性树脂
2018-04-16 热塑性塑料在3D打印市场中一直是很重要的角色,目前ULTEM(聚醚酰亚胺)材料占据了3D打印先进热塑性材料的大部分市场份额,但由于价格较高,一些在增材制造行业技术设备较成熟的制造商,如Stratasys,正努力开发PEEK(聚醚醚酮)和PEKK(聚醚酮酮)类材料逐步替代ULTEM材料。 在刚刚结束的2018年MACH会议上,Stratasys公司在聚醚酮酮的基础上推出了一种新的高性能热塑性塑料―― |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |