| 牌号简介 About |
|---|
| PRE-ELEC® PS 1324是一种基于聚苯乙烯的碳黑填充导电热塑性化合物。除了低电阻率。PRE-ELEC® PS 1324具有良好的机械性能平衡，易于挤压。典型应用包括热成型静电放电托盘的挤压板。 PRE-ELEC® PS 1324 is a carbon black filled conductive thermoplastic compound based on polystyrene. In addition to a low electrical resistivity. PRE-ELEC® PS 1324 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include extruded sheet for thermoformed ESD trays. |
产品描述 Product Description
加工条件：挤出 Extrusion
性能特点： 导电; 易加工; Excellent Processability,Conductive
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.08 | g/cm³ | ASTM D792 |
|
密度 Density |
1.08 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
|
200℃，21.6kg 200℃，21.6kg |
45 | g/10min | ASTM D1238 |
|
200℃，5.0kg 200℃，5.0kg |
0.80 | g/10min | ASTM D1238 |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
200℃，21.6kg 200℃，21.6kg |
45 | g/10min | ISO 1133 |
|
200℃，5.0kg 200℃，5.0kg |
g/10min | ISO 1133 | |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
% | ISO 294-4 | |
|
MD MD |
% | ASTM D955 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A Shaw's A |
ASTM D2240 | ||
|
邵氏 D Shaw's D |
ASTM D2240 | ||
|
邵氏硬度 Shore hardness |
ISO 868 | ||
|
邵氏 A Shaw's A |
ISO 868 | ||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
TD TD |
MPa | ASTM D638 | |
|
MD MD |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
TD，屈服 TD, yield |
MPa | ASTM D638 | |
|
MD，屈服 MD, yield |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
TD，屈服 TD, yield |
MPa | ISO 527-2 | |
|
MD，屈服 MD, yield |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
-- -- 2 |
MPa | ISO 527-2 | |
|
-- -- 3 |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
ASTM D638 | ||
|
TD，屈服 TD, yield |
% | ASTM D638 | |
|
流量，屈服 Flow rate, yield |
% | ASTM D638 | |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
TD，屈服 TD, yield |
% | ISO 527-2 | |
|
流量，屈服 Flow rate, yield |
% | ISO 527-2 | |
|
拉伸应变 Tensile strain |
ASTM D638 | ||
|
断裂 fracture |
% | ASTM D638 | |
|
流量，断裂 Flow rate, fracture |
% | ASTM D638 | |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
断裂 fracture 2 |
% | ISO 527-2 | |
|
断裂 fracture 3 |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
4 mm 4 mm |
MPa | ASTM D790 | |
|
4 mm 4 mm |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 4 |
|||
|
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ASTM D256 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 4 |
|||
|
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
ISO 179 | ||
|
23℃ 23℃ |
ASTM D256 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 4 |
ISO 180 | ||
|
Area Area |
ASTM D256 | ||
|
-20℃，4.00 mm -20℃，4.00 mm |
kJ/m² | ASTM D256 | |
|
23℃，4.00 mm 23℃，4.00 mm |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
|
-20℃，4 mm -20℃，4 mm |
kJ/m² | ASTM D256 | |
|
23℃，4 mm 23℃，4 mm |
kJ/m² | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 4 |
ISO 180 | ||
|
-20℃ -20℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
|
A50 A50 |
℃ | ISO 306/A50 | |
|
Bending Test Bending Test |
|||
|
-- -- 6 |
Cycles | ||
|
-- -- 7 |
Cycles | ||
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ESD STM11.11 | |
|
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
|
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Across Flow |
| 3 Flow |
| 4 4 mm thickness |
| 5 速率 A (50°C/h), 载荷2 (50N) |
| 6 Across Flow, ISO 5626 |
| 7 Flow, ISO 5626 |
|
【新闻资讯】查看全部 
英国密其展现最新静电控制系列产品
2016-12-13 日前在杜塞尔多夫举办的全球最大规模国际塑料与橡胶“K Trade Fair”展会上，英国密其国际公司展示了其系列静电控制技术，包括静电消除和模内贴标等最新产品，以帮助塑料包装及包装印刷行业去处理所面临的众多静电控制问题。 全球包装业模内贴标市场目前正在不断增长。密其新型Hyperion 994CG模内贴标静电发生器带有可调节输出电压性能，减少了总的电能消耗，且体积较小便于安装，适合装配在机械臂前端上，无需高 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付