牌号简介 About |
---|
ULTEM™1000F树脂ULTEM™1000F树脂是一种无定形透明聚醚酰亚胺(PEI)塑料,玻璃化转变温度(Tg)为217°C。 这种固有阻燃树脂具有UL94 V0,V2和5VA等级,符合RoHS,美国FDA和欧盟食品接触标准,NSF 51列表。ULTEM™1000F树脂是一种非增强型通用级产品,具有高耐热性,高强度和高模量以及高温下的广泛耐化学性。 ULTEMTM 1000F resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217?C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS, US FDA and EU Food Contact compliant, with NSF 51 listing. ULTEMTM 1000F resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
337℃,6.6kg 337℃,6.6kg |
9.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.5~0.7 | % | |
吸水率 Water absorption rate |
|||
平衡,23℃ Equilibrium, 23 ℃ |
1.3 | % | ASTM D570 |
24hr 24hr |
0.25 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 3 |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服 yield |
MPa | ASTM D790 | |
泊松比 Poisson's ratio |
ASTM D638 | ||
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
落锤冲击 Drop hammer impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-20~150℃ TD:-20~150℃ |
1/℃ | ASTM E831 | |
MD:-20~150℃ MD:-20~150℃ |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
1.6 mm,在空气中 1.6 mm in air |
kV/mm | ASTM D149 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
2.45 GHz 2.45 GHz |
ASTM D150 | ||
耐电弧性 Arc resistance 6 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率(HVTR) High voltage arc marking rate (HVTR) |
UL 746 | ||
热丝引燃(HWI) Hot wire ignition (HWI) |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
NBS烟雾密度 NBS smoke density |
|||
Flaming,Ds,4 min Flaming,Ds,4 min |
ASTM E662 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
年报预告化工股“独占鳌头”
2022-01-24 2021年在国际大宗原材料价格上涨背景下,化工行业整体呈现高景气。截至2022年1月21日,共有712家A股上市公司披露2021年业绩预告。首批业绩预喜的公司主要扎堆在化工、医药生物、机械 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |