| 牌号简介 About |
|---|
| Fortron® 1140L4 FC是一种40%玻璃纤维增强级产品，是目前可用于食品接触和/或饮用水应用的最强和最坚硬的产品。它具有优异的耐热性和耐化学性，良好的电性能和固有的阻燃性。高温下的高硬度和刚性使得具有良好的承载性能。本产品由于填料含量适中，具有良好的焊接性。这种级别的应用包括电子元件（即线轴、灯罩、刷架）和其他需要强度和耐腐蚀性化学物质的各种组件（即汽车加热器、泵、阀门、燃油轨、微波炉环和蒸馏塔填料）。 Fortron 1140L4 FC is a 40% glass-reinforced grade that is the strongest and toughest product available designed for use in food contact and/or drinking water applications. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. Applications made of this grade are electronical components (i.e. bobbins, lamp housings, brush holders) and various other components requiring strength and resistance to aggressive chemicals (i.e. automotive heaters, pumps, valves, fuel rails, microwave oven rings and distillartion column packings). |
产品描述 Product Description
用途：阀门/阀门部件;泵件;电气/电子应用领域;汽车领域的应用;非特定食品应用;外壳;
性能特点： 防火阻燃等级V-0; 焊接; 机械强度好; 耐化学性; 硬度高; 耐高温; 超高韧性; 阻燃; 电气性好; 防火阻燃等级5VA; 食品接触; Good Rigidity,Good Electrical Properties,Good Hardness,Flame Characteristics,Food contact compliance,High Heat Resistance,Ultra high toughness,Solvent resistance,Welding,V-0,5VA
填料：玻璃纤维 40
| 技术参数 Technical Data | |||
|---|---|---|---|
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
10 | kJ/m² | ISO 179/1eA |
|
23℃ 23℃ |
10 | kJ/m² | ISO 179/1eA |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
53 | kJ/m² | ISO 179/1eU |
|
23℃ 23℃ |
53 | kJ/m² | ISO 179/1eU |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-30℃ -30℃ |
10 | kJ/m² | ISO 180-1A |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
玻璃化转变温度 Glass transition temperature 3 |
℃ | ISO 11357-2 | |
|
熔融温度 Melting temperature 3 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
|
MD MD |
1/℃ | ISO 11359-2 | |
|
TD TD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
|||
|
-- -- |
ohms·cm | ASTM D257 | |
|
-- -- |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
|||
|
1 kHz 1 kHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
|||
|
1 kHz 1 kHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.38 mm 0.38 mm |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Specimen Thickness（Shrinkage） Specimen Thickness（Shrinkage） |
mm | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
M 级 M-level |
ISO 2039-2 | ||
|
拉伸模量 Tensile modulus |
|||
|
-40℃ -40℃ |
MPa | ASTM D638 | |
|
75℃ 75℃ |
MPa | ASTM D638 | |
|
150℃ 150℃ |
MPa | ASTM D638 | |
|
200℃ 200℃ |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength 2 |
MPa | ISO 178 | |
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ASTM D792 , ISO 1183 | |
|
特定体积 Specific volume |
cm³/g | ASTM D792 | |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
% | ASTM D955 | |
|
TD TD |
% | ASTM D955 | |
|
TD TD |
% | ISO 294-4 | |
|
MD MD |
% | ISO 294-4 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
Specific Heat Capacity of Melt Specific Heat Capacity of Melt |
J/kg/℃ | 内部方法 | |
| 备注 |
|---|
| 2 Break |
| 3 10°C/min |
|
【新闻资讯】查看全部 
Acrylates使厨房变得更高档
2020-09-19 搜料网资讯： 厨房，这个空间的意义逐渐在改变。如果说以前的厨房单纯就是做饭的空间的话，最近正逐渐变为边做菜边分享快乐的感性空间。 虽然多少受到最近做菜节目的影响，但生 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |