牌号简介 About |
---|
Solanyl® C8105是一种适用于薄膜应用的端部化合物,专门用于包装。Solanyl® C8105不含淀粉。Solanyl® C8105可在适合(多层)柔性薄膜的传统吹塑或铸膜挤出生产线上加工。Solanyl® C8105的应用包括:T恤袋和垃圾袋。 Solanyl® C8105 is an end compound suitable for film applications and is specially developed for packaging. Solanyl® C8105 is starch free. Solanyl® C8105 can be processed on conventional blown or cast film extrusion lines suitable for (multi-layer) flexible films. Applications in which Solanyl® C8105 can be used are: T-shirt bags & waste bags |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.47 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 到 4.5 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
405 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
16.0 | MPa | ISO 527-2 |
弯曲模量 Bending modulus |
390 | MPa | ISO 178 |
弯曲强度 bending strength |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸模量 Tensile modulus |
|||
MD,20 µm MD,20 µm |
MPa | ||
TD,20 µm TD,20 µm |
MPa | ||
拉伸强度 tensile strength |
|||
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ||
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ||
MD,20 µm MD,20 µm |
MPa | ||
TD,20 µm TD,20 µm |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ||
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
凯柏胶宝:TPE用于婴幼儿的Babynator垫子,实现 "清洁饮食"
2021-06-24 搜料网资讯: 一家位于奥地利的初创公司为婴幼儿开发了一套 学习吃饭的产品,使饮食更加清洁,该公司将凯柏胶宝公司的Thermolast K TPE化合物用于该解决方案的主要组成部分。 Babyna |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |