| Lumicene MPE M 1820 EP是一种以己烯为共聚单体的茂金属基低密度聚乙烯。Lumicene MPE M 1820 EP特别适用于需要优异机械和光学性能的薄膜应用。此外，它还具有良好的低温密封性能。与传统的LLDPE和第一种通用茂金属基聚乙烯相比，Lumicene MPE M 1820 EP的挤出压力低、气泡稳定性好、表观控制能力强。此外，LuMICEN MPE M 1820 EP具有非常低的凝胶水平。应用Lumicene MPE M1820 EP适用于许多应用，如：食品包装层压膜吹塑拉伸膜深冷冻包装FFS袋 Lumicene® mPE M 1820 EP is a Metallocene based Low Density Polyethylene with hexene as comonomer. Lumicene® mPE M 1820 EP is especially dedicated to film applications where outstanding mechanical and optical properties are required. Moreover it offers excellent sealing behavior at low temperature. Lumicene® mPE M 1820 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first general metallocene based polyethylene. Furthermore, Lumicene® mPe M 1820 EP has a very low gel level. Applications Lumicene® mPE M1820 EP is suited for many applications such as: Food Packaging Lamination Film Blown Stretch Film Deep-Freeze Packaging FFS bags |
产品描述 Product Description
用途：薄膜;包装;袋子;食品包装;层压板;吹膜;拉伸缠绕;
加工条件：层压法
性能特点： 耐低温热封性; 低速凝固晶点; 抗氧化; 己烯共聚单体; 良好的测量控制; 光学性能; 低密度; Optical performance,Good Gauge Control,Low speed solidification point,Inoxidizability,Low density,Hexene copolymers,Low temperature heat sealing
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.0 | g/10min | ISO 1133 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
40 | µm | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，40 µm，吹塑薄膜 MD, yield, 40 µ m, blow molded film |
10.0 | MPa | ISO 527-3 |
|
TD，屈服，40 µm，吹塑薄膜 TD, yield, 40 µ m, blow molded film |
10.0 | MPa | ISO 527-3 |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film |
g | ISO 7765-1 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
|
MD：40 µm，吹塑薄膜 MD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
|
TD：40 µm，吹塑薄膜 TD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，40.0 µm，吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
宏达新材控制权拟发生变更 实控人将变更为杭州科立
2021-05-15 搜料网资讯： 5月13日，宏达新材发布公告称，公司接到控股股东上海鸿孜企业发展有限公司(简称上海鸿孜)通知，其将与杭州科立企业管理合伙企业(有限合伙)(简称杭州科立)筹划关于公 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名：搜料网-TOTAL Polyethylene Lumicene® M 1820 EP证书
发送至：（多个地址，中间以逗号隔开）
发送一份副本给我：您还没有填写邮箱!(点击完善资料)
当前牌号已加入对比
支付宝
微信支付