牌号简介 About |
---|
Adflex KS021P是一种反应器TPO(热塑性聚烯烃),采用Lyondellbasell专有的Catalloy工艺技术制造。适用于软膜、片材的挤出压延,聚丙烯的冲击改性,以及单层和多层气冷吹膜。它也被我们的客户用作汽车颜色匹配内饰应用的高耐冷冲击材料。关键特性是柔韧性和耐低温冲击性。该等级为天然颗粒形式。 Adflex KS 021 P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is suitable for the extrusion and calendering of soft film and sheet, for the impact modification of polypropylene, as well as monolayer and multilayer air quenched blown films. It is also used by our customers as high cold impact resistance material for automotive color-matched interior trim applications. Key characteristics are flexibility and low temperature impact resistance. The grade is available in natural pellet form. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.880 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.90 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
38 | ISO 868 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
13.0 | MPa | ISO 527-2/50 |
屈服,23℃ Yield, 23 ℃ |
8.00 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
弦,23℃ String, 23 ℃ 2 |
MPa | ISO 178 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 3 |
kN/m | ASTM D624 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-40℃,局部断裂 -40 ℃, localized fracture |
kJ/m² | ISO 180-1A | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 4 |
ASTM D3763 | ||
-40℃,3.20 mm,Energy at Peak Load,Brittle Failure -40℃,3.20 mm,Energy at Peak Load,Brittle Failure |
J | ASTM D3763 | |
23℃,3.20 mm,Energy at Peak Load,Ductile Failure 23℃,3.20 mm,Energy at Peak Load,Ductile Failure |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 C 模具, 2.0 in/min |
4 21.7 ft/sec |
【新闻资讯】查看全部
重磅!又一央企整合成立!石油行业如何?
2021-12-09 搜料网资讯: 目前央企改革重组已经进入加速通道,中央企业专业化整合再下一城! 经国务院批准,中国物流集团有限公司12月6日正式成立。 这家以综合物流为主业的新央企,以原中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |