牌号简介 About |
---|
HDF895是中分子量高密度聚乙烯级。HDF895特别适合作为低密度聚乙烯/低密度聚乙烯薄膜的混合组分,以提高硬度。应通过适当的性能测试来确定在任何应用中的适用性。 Alkatane HDF895 is a medium molecular weight High Density Polyethylene grade with high stiffness and excellent moisture barrier properties. Film Extrusion: Alkatane HDF895 is particularly suitable for the production of film for the packaging of dry foods where low moisture transmission may allow extended shelf life. Numerous other applications benefit from blending Alkatane HDF895 to enhance the stiffness of LDPE / LLDPE based films, including in the core layer of high clarity coextruded films. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.960 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
18 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD 2% secant, MD |
750 | MPa | ASTM D882 |
2% 正割,TD 2% secant, TD |
780 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709 | |
撕裂强度 tear strength |
ASTM D1922 | ||
MD MD |
cN | ASTM D1922 | |
TD TD |
cN | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫推出新型碳纤维增强PPA牌号,用于轻质高性能部件
2021-02-26 搜料网资讯: 碳纤维增强PPA具有优异的力学性能,可替代铝和镁 适用于汽车结构应用、消费类电子产品和负载工业设备 巴斯夫目前正在扩大其UltramidAdvanced的PPA产品组合,并推出填充物 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |