牌号简介 About |
---|
Valox 357U树脂PBT+PC,UL94V-0/5VA额定值,冲击改性,不透明,未增强,紫外线稳定。应用如筒管、开关和外壳。Valox 357U树脂PBT+PC,UL94V-0/5VA额定值,冲击改性,不透明,未增强,紫外线稳定。诸如线轴、开关和外壳等应用 PBT+PC, UL94V-0/5VA Rated, Impact Modified, Opaque, Unreinforced, UV Stabilized. Applications like bobbins, switches and enclosures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ASTM D792 |
特定体积 Specific volume |
0.750 | cm³/g | ASTM D792 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
8.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD 3 |
1.0 到 1.4 | % | 内部方法 |
MD MD 4 |
0.80 到 1.1 | % | 内部方法 |
TD TD 3 |
% | 内部方法 | |
TD TD 4 |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
耐候性 Weathering resistance |
UL 746C | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
落锤冲击 Drop hammer impact |
ASTM D3029 | ||
23℃ 23℃ 7 |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM E831 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ASTM E831 | |
60 到 138℃ 60 to 138 ℃ |
cm/cm/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance 8 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.46 mm 0.46 mm |
UL 94 | ||
0.64 mm 0.64 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 5 |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 5 |
|||
断裂 fracture 5 |
% | ASTM D638 | |
弯曲模量 Bending modulus 6 |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 |
ASTM D790 | ||
屈服,50 mm跨度 Yield, 50 mm span |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.3 to 4.6 mm |
3 0.75 to 2.3 mm |
4 类型 1, 2,0 in/min |
5 0,051 in/min |
6 Modified |
7 钨电极 |
【新闻资讯】查看全部 ![]()
国家工业节能技术推荐目录(2021)出炉 11项石化化工技术上榜
2021-12-11 搜料网资讯: 为加快推广应用先进适用节能技术、装备和产品, 近期,工业和信息化部发布了《 国家工业节能技术推荐目录(2021) 》(点击下载目录)。共 有包括三效溶剂回收节能 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |