牌号简介 About |
---|
高性能热塑性材料,60%玻璃纤维增强聚醚醚酮(PEEK),半结晶,注射成型颗粒,标准流程,符合FDA食品接触标准,颜色自然/米色。在静态系统中需要更高强度的应用。热膨胀系数低。耐腐蚀环境的化学性,适用于医疗和食品接触应用的灭菌。 High performance thermoplastic material, 60% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliant, colour natural/beige. Applications where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
12 | kJ/m² | ISO 180-A |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃ 23℃ |
50 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
343 | ℃ | ISO 75-2/Af |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
143 | ℃ | ISO 11357 |
熔融温度 Melting temperature Melting temperature |
343 | ℃ | ISO 11357-3 |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
ISO 11359-2 | ||
MD:< 143℃ MD:< 143℃ |
1/℃ | ISO 11359-2 | |
MD:> 143℃ MD:> 143℃ |
1/℃ | ISO 11359-2 | |
TD:< 143℃ TD:< 143℃ |
1/℃ | ISO 11359-2 | |
TD:> 143℃ TD:> 143℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity Thermal conductivity |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | IEC 60093 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
2.5 mm 2.5 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
23 ℃,1 kHz 23 ℃,1 kHz |
IEC 60250 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数GWFI Glow Wire Flammability Index GWFI |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
ISO 868 | ||
拉伸模量 Tensile Modulus Tensile Modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-2 | ||
断裂 brk,23℃ Broken BRK, 23 ℃ |
MPa | ISO 527-2 | |
断裂 brk,125℃ Broken BRK, 125 ℃ |
MPa | ISO 527-2 | |
断裂 brk,175℃ Broken BRK, 175 ℃ |
MPa | ISO 527-2 | |
断裂 brk,275℃ Broken BRK, 275 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,23℃ Broken BRK, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
压缩强度 Compressive Strength Compressive Strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
200℃ 200℃ |
MPa | ISO 604 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 spiral flow length Spiral flow length |
cm | 内部方法 | |
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water Absorption Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
表观粘度 Apparent viscosity Apparent viscosity |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 模具温度: 374°F, 熔体温度: 716°F |
4 380°C nozzle |
5 Onset |
【新闻资讯】查看全部
新概念真空上料零碎的长度较之规范零碎大幅缩短
2016-08-10 一套用于将颗粒料和回用料从储料仓输送至一个台或多个台混料机的新型真空上料系统已经问世,与标准系统相比,它的操作更为简单,并且包括自主控制真空料斗,整体长度比传统上料机和真空料斗短 80%。美奎产品有限公司 (Maguire Products, Inc.) 将在 2016 K展上推出这套系统(10 号馆,A26 展位)。 这款外形小巧的真空料斗LoProTM 恰如其名,其突出特点是仅比混料机盖板高 200 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |