| 牌号简介 About |
|---|
| PLENCO 06553是一种矿物和玻璃纤维增强的两级酚醛模塑料，具有尺寸稳定性，对制动液（如DOT 3和4）具有良好的耐化学性，应提供接近公差的研磨。06553在元件文件E40654下被UL识别。06553提供黑色。06553根据军用规范MIL-M 14（由ASTM D-5948替代）进行了资格鉴定，如果要求和支付费用，可对MFH型和批次进行测试，以证明其符合标准。 PLENCO 06553 is a mineral and glass fiber reinforced two-stage phenolic molding compound, formulated for dimensional stability, good chemical resistance to brake fluids, such as DOT 3 and 4, and should provide grinding to close tolerances. 06553 is UL recognized under component file E40654. 06553 is available in black. 06553 was qualified under military specification MIL-M 14 (superseded by ASTM D-5948) TYPE MFH and batches can, if requested and paid for, be tested for certification to the standard. |
产品描述 Product Description
加工条件：压缩模塑
性能特点： 尺寸稳定性好; 耐化学性; Good Dimensional Stability,Solvent resistance
填料：玻璃纤维/矿物
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
2.12 | g/cm³ | ASTM D792 |
|
表观密度 Apparent density |
1.02 | g/cm³ | ASTM D1895 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.050 | % | ASTM D6289 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.040 | % | ASTM D570 |
|
后收缩 Post contraction |
|||
|
72hr，120℃ 72hr，120℃ |
0.030 | % | ASTM D6289 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
Drop Ball Impact Drop Ball Impact |
J/m | 内部方法 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
连续使用温度 Continuous use temperature |
℃ | ASTM D794 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ASTM E831 | |
|
导热系数 Thermal conductivity coefficient |
|||
|
100℃ 100℃ |
W/m/K | ASTM E1461 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength 3 |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
E 级 E-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
| 备注 |
|---|
| 3、方法A（短时间） |
|
【新闻资讯】查看全部
美国陶氏化学阿克萨集团与维斯塔斯公司签署协议
2017-06-13 美国陶氏化学阿克萨集团预计在其合同期的四年间将提供价值超过3亿美元的碳纤维翼梁帽。 土耳其碳纤维制造商DowAksa(在陶氏化学公司与Aksa公司之间有着50个参与企业)已经完成了与维斯塔斯风系统(丹麦兰讷斯)的长期商业供应协议,这是世界上最大的风力涡轮机供应商,也是碳纤维最大的消费国。DowAksa将使用先进的工艺技术生产碳纤维翼梁帽的层压材料,其将保证为生产更高效、可靠的风力涡轮机提供所需的强度、刚度和重量。 美国陶氏化学阿克萨集团预计在其合同期的四年间 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付