公司信息及水印
牌号简介 About |
---|
一个易于流动,结晶度很好的注塑级,加工速度非常快。生产的零件包括薄壁技术零件(如外壳、配件、握把、小零件和固定夹)。 An easy flowing, finely crystalline injection moulding grade for very fast processing. Parts produced include thin-walled technical parts (eg housing, fittings, grips, small parts and fixing clamps). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,5 kg 275℃,5 kg |
160 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.87 | % | ISO 294-4 |
TD TD |
1.0 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
9.0~10 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
粘度(96% H2SO4) Viscosity (96% H2SO4) |
cm³/g | ISO 307 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.60 mm 1.60 mm |
IEC 60695-11-10 | ||
汽车材料(厚度> = 1mm) Automotive materials (thickness>=1mm) |
FMVSS 302 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
干燥 desiccation |
MPa | ISO 527-1-2 | |
调节后 After adjustment |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,干燥 Yield, drying |
MPa | ISO 527-1-2 | |
调解后 After mediation |
MPa | ISO 527-1-2 | |
拉伸应变 Tensile strain |
|||
屈服,干燥 Yield, drying |
% | ISO 527-1/2 | |
屈服,调解后 Surrender, after mediation |
% | ISO 527-1/2 | |
断裂,干燥 Fracture, drying |
% | ISO 527-1/2 | |
断裂,干燥后 Fracture, after drying |
% | ISO 527-1/2 | |
拉伸蠕变模量(1000 h,应变 <= 0.5%, 23°C) Tensile creep modulus (1000 h, strain<=0.5%, 23 ° C) |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
干燥 desiccation |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,干燥 23 ℃, dry |
kJ/m² | ISO 179/1eU | |
-30℃,干燥 -30 ℃, dry |
kJ/m² | ISO 179/1eU | |
23℃,干燥 23 ℃, dry |
kJ/m² | ISO 179/1eA | |
23℃,调节后 23 ℃, after adjustment |
kJ/m² | ISO 179/1eA | |
-30℃,干燥 -30 ℃, dry |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
ISO 180-A | ||
-30℃ -30℃ |
ISO 180-A | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa 1.8 MPa |
℃ | ISO 75-1/2 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/2 | |
最高使用温度(短期运行) Maximum operating temperature (short-term operation) |
°C | ||
温度指数(50%拉伸强度损失) Temperature index (50% loss of tensile strength) |
|||
5000hrs 5000hrs |
°C | IEC 60216 | |
20000hrs 20000hrs |
°C | IEC 60216 | |
线性膨胀系数(23~80℃) Linear expansion coefficient (23~80 ℃) |
|||
MD MD |
E-6/K | ISO 11359-1/-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | DIN 52612-1 | |
比热容 Specific heat capacity |
J/(kg*K) | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative permittivity |
|||
干燥,1 MHz Dry, 1 MHz |
IEC 60250 | ||
调节后,1 MHz After adjustment, 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz,干燥 1 MHz, dry |
E-4 | IEC 60250 | |
1 MHz,调节后 1 MHz, after adjustment |
E-4 | IEC 60250 | |
体积电阻率 Volume resistivity |
|||
干燥 desiccation |
ohms·cm | IEC 60093 | |
调节后 After adjustment |
ohms·cm | IEC 60093 | |
表面电阻率 Surface resistivity |
|||
调节后 After adjustment |
ohms | IEC 60093 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
IEC 60112 |
备注 |
---|
1 Thickness: >=1mm |
2 一般属性:这些不能被视为规格。 |
3 Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 260°C, TW = 60°C |
4 strain <= 0.5%, 23°C |
5 5000 h |
6 20000 h |
【新闻资讯】查看全部
全球石化市场仍将快速增长
2021-09-22 搜料网资讯: 近日,ChemAnalyst公司发布了《2015~2030石化市场分析报告》。报告显示,2015~2030年,全球石化市场将以年均4.95%的速度快速增长。市场人士表示,塑料、化妆品、药品、太 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |