| 牌号简介 About |
|---|
| Emerge PC/PET 9100CR高级树脂是一种具有优异耐化学性的聚碳酸酯混合物。该等级设计用于医疗设备外壳，可承受反复接触医院常用的各种清洁剂和消毒剂。该等级具有良好的美观性和韧性。主要特点：根据ISO 10993 UL标准对HB应用进行了耐化学性测试：医疗器械外壳或外壳 EMERGE™ PC/PET 9100CR advanced resin is a polycarbonate blend with excellent chemical resistance. This grade was designed for use in medical equipment housings and can withstand repeated exposure to a variety of cleaners and disinfectants commonly used in hospitals. This grade has good aesthetics and excellent toughness. Main Characteristics: Excellent chemical resistance Tested under ISO 10993 UL listing for HB Applications: Medical device housings or enclosures |
产品描述 Product Description
用途：医疗/护理用品;电器外壳;外壳;
加工条件：注射成型 Injection Molding
性能特点： 耐化学性; 生物兼容性; 韧性好; 表面光泽度好; Good flexibility,Good surface appearance,Biocompatible,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.23 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
260℃，5.0kg 260℃，5.0kg |
8.5 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.60 到 0.90 | % | |
|
TD TD |
0.50 到 0.80 | % | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-30℃，3.2mm，注塑成型 -30 ℃, 3.2mm, injection molding |
750 | J/m | |
|
23℃，3.2mm，注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
-40℃，3.20 mm，注塑，Peak Energy -40 ℃, 3.20 mm, injection molded, Peak Energy |
J | ||
|
-40℃，3.20 mm，注塑，Total Energy -40 ℃, 3.20 mm, injection molded, Total Energy |
J | ||
|
23℃，3.20 mm，注塑，Peak Energy 23 ℃, 3.20 mm, injection molded, Peak Energy |
J | ||
|
23℃，3.20 mm，注塑，总能量 23 ℃, 3.20 mm, injection molding, total energy |
J | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ||
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 7 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
|||
|
1.6 mm，在油中 1.6 mm in oil |
kV/mm | ||
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | ||
|
相对电容率 Relative permittivity |
|||
|
100 Hz 100 Hz |
|||
|
1 MHz 1 MHz |
|||
|
耗散因数 Dissipation factor |
|||
|
100 Hz 100 Hz |
|||
|
1 MHz 1 MHz |
|||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.00 mm 1.00 mm 8 |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级，3.20 mm R-grade, 3.20 mm |
ASTM D785 | ||
|
拉伸模量 Tensile modulus 4 |
|||
|
3.20 mm，注塑成型 3.20 mm, injection molded 4 |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength 5 |
|||
|
屈服，3.20 mm，注塑成型 Yield, 3.20 mm, injection molding |
MPa | ||
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ||
|
拉伸应变 Tensile strain 5 |
|||
|
屈服，3.20 mm，注塑成型 Yield, 3.20 mm, injection molding |
% | ||
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
% | ||
|
弯曲模量 Bending modulus 6 |
|||
|
3.20 mm，注塑成型 3.20 mm, injection molded 6 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 6 |
|||
|
3.20 mm，注塑成型 3.20 mm, injection molded 6 |
MPa | ASTM D790 | |
| 备注 |
|---|
| 3、Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
| 4、5.0 mm/min |
| 5、50 mm/min |
| 6、1.3 mm/min |
| 7、标准 B (120°C/h), 压 力1 (10N) |
| 8、这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
|
【新闻资讯】查看全部 
化销华东太阳能背板膜用聚酯切片销量创新高
2020-12-16 搜料网资讯： 今年以来，化销华东持续攻坚创效，在助力产业链升级方面下功夫，聚焦产业链高精尖，太阳能背板膜级专用聚酯切片销量创新高，1-11月销售6.06万吨，较去年同期增长6 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付