牌号简介 About |
---|
耐高温强度在高温下优越的机械性能高抗压强度和抗蠕变性能优异的化学性能优越的耐等离子腐蚀性能优异的电气性能耐磨、低摩擦、自润滑、对配合件无磨损、极低的吸湿性。在不变形的情况下,在负载和温度下,抗辐射兼容,非常低的出气率,零金属和矿物可萃取物,在X、Y和Z方向上极为稳定的尺寸相等CTE。 High temperature resistance Strength at elevated temperature Superior mechanical properties High compressive strength and creep resistance Excellent chemical resistance Superior resistance to plasma etching Outstanding electrical properties Wear resistance, low friction, self-lubricating Non-abrasive to mating parts Extremely low moisture absorption Radiation resistant Compliant without deforming under load and temperature Very low outgassing Zero metal and mineral extractables Extremely dimensionally stable Equal CTE in X, Y and Z directions |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.47 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
饱和 saturated |
< 0.10 | % | ASTM D570 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
4.0E-5 | 1/℃ | ASTM D696 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
1.0E+10 到 1.0E+11 | ohms | ASTM D257 |
体积电阻率 Volume resistivity |
1.0E+12 到 1.0E+13 | ohms·cm | ASTM D257 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空间稳定性 Spatial stability |
|||
收缩,24 hrs,260℃ Shrinkage, 24 hours, 260 ℃ |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
E 级 E-level |
ASTM D785 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
-- -- |
MPa | ASTM D638 | |
260℃ 260℃ 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂 fracture |
% | ASTM D638 | |
断裂,260℃ Fracture, 260 ℃ 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
-- -- |
MPa | ASTM D790 | |
100% 应变 100% strain 2 |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
ASTM D695 | ||
260℃ 260℃ 2 |
MPa | ASTM D695 | |
100% 应变 100% strain |
MPa | ASTM D695 | |
Wear Rate - Jet Engine Simulation Testing,Bearing Wear Rate - Jet Engine Simulation Testing,Bearing |
|||
260℃ 260℃ |
µm | ||
345℃ 345℃ |
µm | ||
400℃ 400℃ |
µm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 15 min soak |
【新闻资讯】查看全部
“千亿件”时代来临 快递物流业开“打”价值战
2022-01-21 搜料网资讯: 2021年,我国快递业务量预计将达1085亿件;2022年,有望再创1225亿件的新高,同比增长13%。与此同时,在中国物流与采购联合会发布的50强榜单中,民营50强物流企业门槛升 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |