牌号简介 About |
---|
HWB-554是一种经认证的优质己烯共聚物高分子量,开发用于高性能中大型工业容器的吹塑成型。HWB-554具有较高的膨胀率、一致的加工性能、ESCR的优异组合、冲击强度、刚度、抗蠕变和优异的耐化学性。HWB-554应用包括55加仑的圆桶、船运集装箱、工业罐、农用化学品、汽车零件、工具箱、手提箱、运动用品、滑雪板和行李车箱。HWB-554建议的加工温度为210至230°C。HWB-554符合FDA法规21CFR 177.1520(c)3.2(a)和大多数有关使用聚乙烯与食品接触的国际法规。 HWB-554 is a certified prime grade Hexene copolymer High Molecular Weight developed for BLOW MOLDING of high performance medium to large size industrial containers. HWB-554 features High-Swell, consistent processability, outstanding combination of ESCR, Impact strength, Stiffness, Creep resistance, and excellent chemical resistance. HWB-554 applications include 55 gallon drums, shipping containers, industrial tanks, agrochemicals, automotive parts, tool boxes, carrying cases, sport articles, ski and baggage car boxes. HWB-554 recommended processing temperature is 210 to 230°C.. HWB-554 complies with FDA regulation 21CFR 177.1520 (c) 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.954 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.028 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
5.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
模压成型,F50 Molded into shape, F50 |
> 1000 | hr | ASTM D1693 |
50 ℃,1.75 mm,10%非离子表面活性剂,模压成型,F50 50 ℃, 1.75 mm, 10% non-ionic surfactant, molded, F50 2 |
45.0 | hr | ASTM D1693B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,模压成型 Yield, molding 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂,模压成型 Fracture, molded 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
1% 正割,模压成型 1% cut, molded 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吹气模制温度 Blowing molding temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Notched Bent Strip |
3 2.0 in/min |
4 0.051 in/min |
【新闻资讯】查看全部
废旧塑料通常采用热解油化技术加以回收再使用
2015-11-23 由于近些年来,国内的废塑料市场一直存在着不良的现象,比如说有一些企业进行非法加工废塑料之后,直接投放到国内市场上进行销售等等诸如没有经过严格的检查就重新利用的废塑料,所以近期国内纷纷对废塑料进行了严格的审查。 由吉林发改委和吉林工商部门联合组成的执法小组深入到吉林塑料销售市场,突击检查废塑料的相关情况,并依法对违规塑料企业和经营商户进行相应的处罚。 从吉林相关部门了解到,吉林各地工商行政管理部门已对拒不执行塑料加工标准的商业企业和个体工商业户进行了处罚,罚没 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |