牌号简介 About |
---|
HEPLA®H2000是一种无增强聚苯醚(PPE)产品。其特点包括:符合RoHS标准。一种新的高流量设计,适用于配电箱、继电器箱和接线盒等地下应用。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.1 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
24 hr, 23℃, 50% RH 24 hr, 23℃, 50% RH |
0.39 | % | ISO 62 |
24 hr, 23℃ 24 hr, 23℃ |
2 | % | ISO 62 |
收缩率 Shrinkage rate |
|||
MD: 24 hr MD: 24 hr |
1.4 to 1.7 | % | ASTM D955 |
TD:24 hr TD:24 hr |
1.2 to 1.5 | % | ASTM D955 |
熔体质量流动速率 Melt Flow Rate |
|||
280℃,2.16 kg 280℃,2.16 kg |
g/10 min | ASTM D1238 | |
280℃,5.0 kg 280℃,5.0 kg |
g/10 min | ASTM D1238 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
50 mm/min 50 mm/min |
MPa | ASTM D638 | |
Tensile Stress, yield, Type I Tensile Stress, yield, Type I |
|||
5.0 mm/min 5.0 mm/min |
MPa | ASTM D638 | |
Tensile Stress, break, Type I Tensile Stress, break, Type I |
|||
5.0 mm/min 5.0 mm/min |
MPa | ASTM D638 | |
Tensile Strain, yield, Type I Tensile Strain, yield, Type I |
|||
5.0 mm/min 5.0 mm/min |
% | ASTM D638 | |
Tensile Strain, break, Type I Tensile Strain, break, Type I |
|||
5.0 mm/min 5.0 mm/min |
% | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
2.0 mm/min 2.0 mm/min |
MPa | ISO 178 | |
100 mm Span, 2.6 mm/min 100 mm Span, 2.6 mm/min |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,2.0 mm/min Yield, 2.0 mm/min |
MPa | ISO 178 | |
断裂,100 mm Span, 1.3 mm/min Fracture, 100 mm Span, 1.3 mm/min |
|||
Flexural Stress, break Flexural Stress, break |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Charpy Notched Izod Impact Charpy Notched Izod Impact |
|||
23℃ 23℃ |
kJ/m2 | ISO 179/2C | |
-20℃ -20℃ |
kJ/m2 | ISO 179/2C | |
悬臂梁缺口冲击强度, 23℃ Impact strength of cantilever beam notch, 23 ℃ |
J/m | ASTM D256 | |
Notched Izod Impact, -30℃ Notched Izod Impact, -30℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
80*10*4 , 23℃ 80*10*4 , 23℃ |
kJ/m2 | ISO 180/4A | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
80*10*4 ,-30℃ 80*10*4 ,-30℃ |
kJ/m2 | ISO 180/4A | |
Instrumented Dart Impact, -30℃ Instrumented Dart Impact, -30℃ |
|||
Energy at Peak Load Energy at Peak Load |
J/m | ASTM D3763 | |
Instrumented Dart Impact, 23℃ Instrumented Dart Impact, 23℃ |
|||
Energy at Peak Load Energy at Peak Load |
J/m | ASTM D3763 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
1.60 mm,在油中 1.60 mm in oil |
kV/mm | ASTM D149 | |
耗散因数1 MHz Dissipation factor 1 MHz |
ASTM D150 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,100 mm Span, 120*10*4 mm 0.45 MPa, unannealed, 100 mm Span, 120 * 10 * 4 mm |
℃ | ISO 75-2/Be | |
0.45 MPa, Unannealed, 6.40 mm 0.45 MPa, Unannealed, 6.40 mm |
℃ | ASTM D648 | |
CLTE - Flow (-40 to 40℃) CLTE - Flow (-40 to 40℃) |
1/℃ | ASTM E831 | |
CLTE - Flow (60 to 138℃) CLTE - Flow (60 to 138℃) |
1/℃ | ASTM E831 | |
CLTE - Transverse (-40 to 40℃) CLTE - Transverse (-40 to 40℃) |
1/℃ | ASTM E831 | |
CLTE - Transverse (60 to 138℃) CLTE - Transverse (60 to 138℃) |
1/℃ | ASTM E831 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部 ![]()
晶科能源光伏组件获碳足迹证书
2021-11-07 搜料网资讯: 近日,国际独立第三方检测、检验和认证机构德国莱茵TUV大中华区(以下简称TUV莱茵)为晶科能源控股有限公司(以下简称晶科能源)两款主打光伏组件产品(163系列和182系列)颁 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |