牌号简介 About |
---|
SABIC® PP CX02-82是一种发射优化的高结晶共聚物。它具有高刚度、完美平衡、高热尺寸稳定性、抗冲击性和流动性。这种材料也具有良好的美学性能,通常用于汽车内饰应用。它是传统滑石填充共聚物的明显替代品,具有相当大的重量节省优势。SABIC® PP CX02-82是指定的汽车等级。 SABIC® PP CX02-82 is an emission optimised high crystalline copolymer. It offers high stiffness, in perfect balance with high thermal dimensional stability, impact resistance and flow. This material has excellent aesthetic properties as well and is typically used for automotive interior applications. It is the obvious alternative to conventional talc-filled copolymers, offering considerable weight saving advantage. SABIC® PP CX02-82 is a designated automotive grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
15 | g/10min | ASTM D1238,ISO 1133 |
收缩率 Shrinkage rate |
内部方法 | ||
MD:24 hrs MD:24 hrs |
1.6 | % | |
24 hrs 24 hrs |
1.6 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
0℃,注塑成型 0 ℃, injection molding |
8.0 | kJ/m² | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-20℃,注塑成型 -20 ℃, injection molding |
J/m | ASTM D256-A | |
0℃,注塑成型 0 ℃, injection molding |
J/m | ASTM D256-A | |
23℃,注塑成型 23 ℃, injection molding |
J/m | ASTM D256-A | |
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-1A | |
0℃,注塑成型 0 ℃, injection molding |
kJ/m² | ISO 180-1A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525,ISO 306/A120 4 4 | |
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 5 5 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
碳排放 carbon emission |
µg/g | VDA 277 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
1% 正割,注塑成型 1% cut, injection molding 1 |
MPa | ASTM D638 | |
注塑成型 injection molding |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding 2 |
MPa | ASTM D638 | |
屈服,注塑成型 Yield, injection molding |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding 3 |
% | ASTM D638 | |
屈服,注塑成型 Yield, injection molding |
% | ISO 527-2/1A/50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 2.0 in/min |
4 标准 B (120°C/h), 压 力1 (10N) |
5 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
签约140亿元!中企中海油服与中东石油公司签署多份长期合同
2022-10-26 扫描上图二维码,可以免费下载 搜料 APP 10月23日,中海油田服务股份有限公司(下称中海油服)宣布,公司近期在海外市场取得重大突破。该公司已与中东地区领先的国际石油公司签订了 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |