| 牌号简介 About |
|---|
| Adiprene Duracast C900是一种具有低游离MDI含量的MDI端接聚己内酯预聚物。将该预聚物与Duracure C3或C3-LF进行扩链，得到了物理性能优良的高性能90A弹性体。其他优点是改进了加工特性，在搬运过程中更容易管理健康和安全。低游离MDI预聚物的独特性能组合优于TDI和传统MDI预聚物。硬脑膜预聚物用硬脑膜C3或C3-LF固化，提供了一个优越的硬段，并提供了独特的加工和生产力的提高。这种高性能硬段具有优异的物理和工程性能，包括高抗切割和撕裂性、改进的弯曲疲劳、低温柔性、优异的动力学（低温和高温下）和其他高温性能。传统上，胺固化剂不能与MDI预聚物一起使用，因为它们具有高反应性（短的使用寿命），即使它们具有一些性能优势，如耐高温性和撕裂性能。它还提供了EH&S的优势，因为它基于低游离单体技术，是一个无MBOCA系统。 ADIPRENE DURACAST C900 is an MDI-terminated polycaprolactone prepolymer having low free MDI content. A high performance 90A elastomer with excellent physical properties is obtained when this prepolymer is chain extended with DURACURE™ C3 or C3-LF. Other advantages are improved processing characteristics and easier management of health & safety during handling. The unique combination of properties exhibited by low free MDI prepolymers is superior to those available from TDI and conventional MDI prepolymers. DURACAST prepolymers cured with DURACURE C3 or C3-LF provide a superior hard segment and offer unique processing and productivity improvements. This high performance hard segment offers excellent physical and engineering properties, including high cut and tear resistance, improved flex fatigue, low temperature flexibility, excellent dynamics (at both low and high temperatures) and other high temperature properties. Traditionally, amine cures could not be used with MDI prepolymers due to high reactivity (short pot life) even though they offer some performance advantages such as high temperature resistance and tear properties. It also offers EH&S advantages as it is based on low free monomer technology and is a MBOCA free system. |
产品描述 Product Description
性能特点： 耐低温柔性; 机械强度好-撕裂; 加热硫化; Baking,Low temperature toughness,Good tear strength
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density 2 |
1.13 | g/cm³ | ASTM D792 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
裤型撕裂耐性 Pant tear resistance |
ASTM D1938 | ||
|
-- -- 2 |
33.3 | N/mm | ASTM D1938 |
|
-- -- 3 |
42.7 | N/mm | ASTM D1938 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸应力 Tensile stress |
|||
|
100% 应变 100% strain |
6.17 | MPa | ASTM D412 |
|
100% 应变 100% strain |
6.29 | MPa | ASTM D412 |
|
300% 应变 300% strain |
MPa | ASTM D412 | |
|
300% 应变 300% strain |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
-- -- 2 |
MPa | ASTM D412 | |
|
-- -- 3 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂 fracture 2 |
% | ASTM D412 | |
|
断裂 fracture 3 |
% | ASTM D412 | |
|
撕裂强度 tear strength |
|||
|
-- -- 4 , 2 |
kN/m | ASTM D624 | |
|
-- -- 4 , 3 |
kN/m | ASTM D624 | |
|
开裂 cracking 2 |
kN/m | ASTM D470 | |
|
开裂 cracking 3 |
kN/m | ASTM D470 | |
|
压缩形变 Compression deformation |
ASTM D395B | ||
|
70℃，22 hr 70℃，22 hr 2 |
% | ASTM D395B | |
|
70℃，22 hr 70℃，22 hr 3 |
% | ASTM D395B | |
|
100℃，22 hr 100℃，22 hr 2 |
% | ASTM D395B | |
|
100℃，22 hr 100℃，22 hr 3 |
% | ASTM D395B | |
|
巴肖氏弹性 Basho's elasticity |
ASTM D2632 | ||
|
-- -- 3 |
% | ASTM D2632 | |
|
回弹性 - Drop Ball Resilience - Drop Ball |
|||
|
-- -- 2 |
% | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
储存稳定性 storage stability |
|||
|
50 ℃ 50 ℃ |
min | ||
|
70 ℃ 70 ℃ |
min | ||
|
脱模时间 stripping time |
|||
|
120℃ 120℃ |
min | ||
|
140℃ 140℃ |
min | ||
|
后固化时间 Post curing time |
|||
|
120℃ 120℃ 5 |
hr | ||
|
140℃ 140℃ 6 |
hr | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient |
|||
|
DIN DIN 2 |
|||
|
DIN DIN 3 |
|||
|
NBS NBS 2 |
% | ||
|
NBS NBS 3 |
% | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A Shaw's A 2 |
ASTM D2240 | ||
|
邵氏 A Shaw's A 3 |
ASTM D2240 | ||
|
磨损量 - Relative vol loss Relative vol loss |
|||
|
-- -- 2 |
mm³ | ||
|
-- -- 3 |
mm³ | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Post cure 140°C (24 hrs.) |
| 3 Post cure 120°C (24 hrs.) |
| 4 C 模具 |
| 5 Standard |
| 6 High Performance |
|
【新闻资讯】查看全部 
中国家电全面登陆越南市场
2021-04-27 搜料网资讯： 据韩国环球经济网近日报道，在越南家电市场上，东芝、松下、夏普等日本家电产品逐渐消失，而相对物美价廉的中国家电产品正在取代这一位置。 近日，越南4大IT及电子 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付