| 牌号简介 About |
|---|
| ADVANCENE™ EM-2420-AAB线性低密度聚乙烯（LLDPE）树脂采用先进的气相聚乙烯工艺生产，用于一般用途的注塑应用。该树脂具有优异的抗冲击强度、刚度、耐环境应力、抗裂性和加工性能。主要特点：注塑成型。通用应用。优异的低温冲击强度、刚度、抗裂性和加工性。分子量分布非常窄。 ADVANCENE™ EM-2420-AAB Linear Low Density Polyethylene (LLDPE) Resin is produced using advanced gas phase PE process and is intended for use in general purpose injection molding applications. This resin has been designed to have excellent impact strength, rigidity, environmental stress crack resistance and processability. Main Charactelistics : Injection molding. General purpose applications. Excellent low temperature impact strength, rigidity, stress crack resistance and processability. Very narrow molecular weight distribution. |
产品描述 Product Description
用途：通用;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 耐低温冲击; 窄分子量分布; 冲击性能好; 抗应力开裂; 低密度; 易加工; Good Rigidity,Excellent Processability,High impact resistance,Weight distribution,Low density,low-temperature impact resistance,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.924 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
20 | g/10min | ASTM D1238 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
50 ℃，100%非离子表面活性剂，F50 50 ℃, 100% non-ionic surfactant, F50 |
20.0 | hr | ASTM D1693 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸冲击强度 Tensile impact strength |
|||
|
-- -- 2 |
168 | kJ/m² | ASTM D1822 |
|
-- -- |
168 | kJ/m² | ISO 8256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
结晶峰温度 Crystallization peak temperature |
|||
|
DSC DSC |
℃ | ASTM D3418 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ASTM D2240 | ||
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ||
|
断裂 fracture |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ||
|
断裂 fracture |
% | ||
|
弯曲模量 Bending modulus |
|||
|
2% 正割 2% secant |
MPa | ASTM D790-B | |
| 备注 |
|---|
| 2、Type S |
|
【新闻资讯】查看全部 
扬州惠通10.5万吨聚乳酸项目环评获批 一期产能3.5万吨
2022-04-15 可降解可循环中心获悉，4月13日，扬州惠通生物新材料有限公司（以下简称惠通新材）年产10.5万吨聚乳酸的生物可降解塑料及其系列产品研发生产项目环境影响报告书的通过批复。 项 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付