公司信息及水印
牌号简介 About |
---|
一种柔软的、可染色的无卤阻燃(HFFR)SEBS基热塑性弹性体(TPE)化合物,具有优异的抗紫外线性能。可粘合:PP、EVA、PE A soft, colorable, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
0.948 | g/cm³ | ASTM D792 |
-- -- |
0.950 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃,2.00 mm Shore A, 15 seconds, 23 ℃, 2.00 mm |
75 | ISO 868 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
7.50 | MPa | ASTM D412, ISO 37 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
2.90 | MPa | ASTM D412, ISO 37 |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ASTM D412,ISO 37 | |
撕裂强度 tear strength |
|||
TD,23℃ TD,23℃ |
kN/m | ASTM D624 | |
TD,23℃ TD,23℃ |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573, ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573, ISO 188 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
|||
支撐 A,150℃,168 hr Support A, 150 ℃, 168 hr |
ASTM D573, ISO 188 | ||
空气中质量的变化 Changes in air quality |
|||
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471, ISO 1817 | ||
23℃,168 hr,在15%氯化钠中 23 ℃, 168 hr, in 15% sodium chloride |
% | ||
23℃,168 hr,在50%氢氧化钠中 23 ℃, 168 hr, in 50% sodium hydroxide |
% | ||
23℃,168 hr,在98%硫酸中 23 ℃, 168 hr, in 98% sulfuric acid |
% | ||
23℃,168 hr,在IRM 903油中 23 ℃, 168 hr, in IRM 903 oil |
% | ||
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ||
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471, ISO 1817 | ||
23℃,168 hr,在15%氯化钠中 23 ℃, 168 hr, in 15% sodium chloride |
% | ||
23℃,168 hr,在50%氢氧化钠中 23 ℃, 168 hr, in 50% sodium hydroxide |
% | ||
23℃,168 hr,在98%硫酸中 23 ℃, 168 hr, in 98% sulfuric acid |
% | ||
23℃,168 hr,在IRM 903油中 23 ℃, 168 hr, in IRM 903 oil |
% | ||
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
|||
支撐 A,23℃,168 hr,在15%氯化钠中 Support A, 23 ℃, 168 hr, in 15% sodium chloride |
ASTM D471 | ||
支撐 A,23℃,168 hr,在50%氢氧化钠中 Support A, 23 ℃, 168 hr, in 50% sodium hydroxide |
ASTM D471 | ||
支撐 A,23℃,168 hr,在98%硫酸中 Support A, 23 ℃, 168 hr, in 98% sulfuric acid |
ASTM D471 | ||
支撐 A,23℃,168 hr,在IRM 903油中 Support A, 23 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
支撐 A,23℃,168 hr,在水中 Support A, 23 ℃, 168 hr, in water |
ASTM D471, ISO 1817 | ||
支撐 A,23℃,168 hr,在 15% 氯化钠中 Support A, 23 ℃, 168 hr, in 15% sodium chloride |
ISO 1817 | ||
支撐 A,23℃,168 hr,在 50% 氢氧化钠中 Support A, 23 ℃, 168 hr, in 50% sodium hydroxide |
ISO 1817 | ||
支撐 A,23℃,168 hr,在 98% 硫酸中 Support A, 23 ℃, 168 hr, in 98% sulfuric acid |
ISO 1817 | ||
支撐 A,23℃,168 hr,在 IRM 903 油中 Support A, 23 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
质量变化率 Quality change rate |
ASTM D471 | ||
23℃,168 hr,在15%氯化钠中 23 ℃, 168 hr, in 15% sodium chloride |
% | ||
23℃,168 hr,在50%氢氧化钠中 23 ℃, 168 hr, in 50% sodium hydroxide |
% | ||
23℃,168 hr,在98%硫酸中 23 ℃, 168 hr, in 98% sulfuric acid |
% | ||
23℃,168 hr,在IRM 903油中 23 ℃, 168 hr, in IRM 903 oil |
% | ||
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ||
质量变化率 Quality change rate |
ISO 1817 | ||
23.0℃,168 hr,在50%氢氧化钠中 23.0 ℃, 168 hr, in 50% sodium hydroxide |
% | ||
23.0℃,168 hr,在水中 23.0 ℃, 168 hours in water |
% | ||
23.0℃,168 hr,在15%氯化钠中 23.0 ℃, 168 hr, in 15% sodium chloride |
% | ||
23.0℃,168 hr,在98%硫酸中 23.0 ℃, 168 hr, in 98% sulfuric acid |
% | ||
23.0℃,168 hr,在IRM 903油中 23.0 ℃, 168 hr, in IRM 903 oil |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746,ISO 812 | |
相对温度指数 Relative temperature index |
UL 746 | ||
电气性能 Electrical performance |
℃ | UL 746 | |
1.10 mm 1.10 mm |
℃ | ||
1.60 mm 1.60 mm |
℃ | ||
3.00 mm 3.00 mm |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高压电弧抗点燃指数(HVAR)(PLC) High voltage arc ignition resistance index (HVAR) (PLC) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.60 mm 1.60 mm |
|||
3.00 mm 3.00 mm |
|||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.10 mm 1.10 mm |
|||
1.60 mm 1.60 mm |
|||
3.00 mm 3.00 mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
耐克、阿迪股价大跌,明星终止合作霸屏热搜,原来它们在中国赚了这
2021-03-26 搜料网资讯: HM集团一份碰瓷新疆棉花的声明,激怒了中国民众,引发舆论广泛关注。 随着事件的发酵,不少外国企业被发现近两年发表过与新疆棉花切割言论,其中包括BCI成员巴宝莉 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |