牌号简介 About |
---|
Lucofin1400-HN粉末是一种极性共聚物,由乙烯和丙烯酸丁酯组成,结晶度较低。由于其化学结构,Lucofin 1400 HN粉末比密度相当的乙烯均聚物更软、更灵活。Lucofin 1400 HN粉末未着色,不含添加剂颗粒。Lucofin® 1400HN Powder可用于聚合物改性和改善:对于化合物,矿物、填料、颜料和添加剂的相容性和吸收能力沥青中的耐热性,不影响冷弹性产品的优越性,柔韧性,耐低温冲击强度(-40°C)热稳定性。R(无腐蚀性副产品)良好的机械性能高端使用温度良好的兼容性和填料验收良好的感官环境良好的耐热性应用Lucofin® 1400HN Powder可用于以下应用:用作聚合物改性沥青和粉末涂料用沥青化合物的支撑材料 Lucofin 1400 HN Powder is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin 1400 HN Powder is softer and more flexible than ethylene homopolymeres with comparable density. Lucofin 1400 HN Powder is supplied as uncoloured and without additives granules. Lucofin 1400HN Powder can be used for polymer modification and improve: for compounds, the compatibility and absorptive capacity of minerals, fillers, pigments and additives the heat resistance in bitumen, without negative influence on the cold flexibility Product advantages flexibility impact strength at low temperatures (- 40 °C) thermal stability of polymer (no corrosive by products) good mechanical properties high end use temperature good compatibility and filler acceptance good organoleptics environmentally sound heat resistance Applications Lucofin 1400HN Powder can be used in the following applications: as supporting material for compounds for polymer modification of bitumen and asphalt for powder coating |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.4 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) 2 |
|||
F0 F0 2 |
> 1000 | hr | ASTM D1693 |
颗粒大小 Particle size |
500 | µm | ASTM D1921 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
70.0 | ℃ | ISO 306/A50 |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Comonomer BA Comonomer BA |
% | DIN 51451 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 D Shaw's D |
ISO 868 | ||
球压硬度 Ball hardness |
|||
H 49/30 H 49/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 IEC 538 |
【新闻资讯】查看全部
墨西哥Grupo Ortiz利用新的史太林格设备扩大拉菲塑编袋生产
2021-09-28 搜料网资讯: 尽管墨西哥疫情导致供应链中断,但拉丁美洲塑料行业最大的参与者Grupo Ortiz(GO)仍在大力投资其多方面的塑料加工业务。目前,该公司正在墨西哥西部莫雷利亚建造一座 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |