牌号简介 About |
---|
Ebarta GM 976是一种易于操作的双组分聚氨酯浇注料,与型砂相比,它具有很低的粘合性能。由于其非常高的耐磨性,GM 976特别适用于铸造模式,这些模式必须抵抗由型砂造成的磨损。GM 976甚至在使用高温型砂时保持了较高的机械强度。应用芯盒铸造型好的浇注料性能耐磨性好的抗压强度 ebalta GM 976 is an easy-to-handle-2 components-polyurethane casting compound which shows very low adhesive properties compared to moulding sand. Due to its very high abrasion resistance, GM 976 is especially suitable for foundry patterns, which have to resist to abrasive wear by moulded sand. GM 976 even keeps its high mechanical strength when using moulding sands with higher temperatures. Applications Core boxes Foundry pattern well castable Properties abrasion resistant good compressive strength |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
8.0 到 12 | kJ/m² | ISO 179 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
1.55 到 1.65 | g/cm³ | |
粘度 viscosity |
|||
25℃ 25℃ |
3.5 到 4.5 | Pa·s | |
固化时间 Curing time |
|||
20℃ 20℃ |
4.0 到 10 | hr | |
储存稳定性 storage stability 2 |
|||
20 ℃ 20 ℃ 2 |
25 到 35 | min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 7619 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 200 g |
【新闻资讯】查看全部
停产搬迁!鲁西化工3家子公司累计获赔18.1亿
2019-12-27 12月25日晚间,鲁西化工发布了关于签订收回 二厂及原四厂 国有土地使用权协议的公告。 公告表示,根据聊城市委、市政府安排,因城市规划调整及公共利益需要,鲁西化工集团股份有 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |