牌号简介 About |
---|
Bayflex 906是一种由两种液体成分组成的全复合、水吹、聚醚型聚氨酯系统。A组分为改性二苯基甲烷二异氰酸酯(MDI)预聚物,B组分为聚醚多元醇体系。Bayflex 906系统开发用于需要微孔芯和坚硬耐磨外表面的各种应用。可能的应用实例包括设备手柄、办公椅扶手和衬垫条。与任何产品一样,用户必须在给定应用程序中测试Bayflex 906系统的使用(包括但不限于现场测试),以确定适用性。 Bayflex 906 is a fully compounded, water-blown, polyether-based polyurethane system consisting of two liquid components. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. Bayflex 906 system was developed for use in a wide variety of applications requiring a microcellular core and a tough, abrasion-resistant outer surface. Examples of possible applications include appliance handles, office chair armrests, and dunnage strips. As with any product, use of the Bayflex 906 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,12.7 mm Shaw A, 12.7 mm |
75 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,12.70 mm Fracture, 12.70 mm |
5.65 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂,12.70 mm Fracture, 12.70 mm |
200 | % | ASTM D412 |
撕裂强度 tear strength 2 |
|||
12.7 mm 12.7 mm 2 |
27.5 | kN/m | ASTM D624 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components 3 |
|||
部件 A Component A |
按重量计算的混合比: 73 | ||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 98 Index |
【新闻资讯】查看全部
俄乌局势加剧零部件短缺,多家汽车制造商部分工厂停产减产
2022-03-04 汽车制造业尚未从芯片短缺、新冠疫情中完全恢复,俄乌局势又给其欧洲地区供应链带来重挫。 汽车线束电缆供应商莱尼(Leoni)在乌克兰有两家工厂,该公司表示正在加紧通过增加其 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |