牌号简介 About |
---|
高性能热塑性材料,聚芳醚酮(PAEK),半结晶,注射成型颗粒,标准流程,用磨损添加剂加固,颜色为黑色。WG102不含聚四氟乙烯(PTFE)或其他卤化添加剂。高温摩擦学应用于高强度和高刚度。耐磨性好,摩擦系数低,热膨胀系数低。抗腐蚀环境的化学反应。 High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, granules for injection moulding, standard flow, reinforced with wear additives, colour black. WG102 does not contain polytetrafluoroethylene (PTFE) or other halogenated additives. Higher temperature tribological applications for high strength and stiffness. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃ 23℃ |
5.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
35 | kJ/m² | ISO 179/1U |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
6.0 | kJ/m² | ISO 180-A |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃ 23℃ |
40 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
367 | ℃ | ISO 75-2/Af |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
ISO 11357-2 | ||
-- -- |
℃ | ISO 11357-2 | |
-- -- |
℃ | ISO 11357-2 | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
ISO 11359-2 | ||
MD:< 143℃ MD:< 143℃ |
1/℃ | ISO 11359-2 | |
MD:> 143℃ MD:> 143℃ |
1/℃ | ISO 11359-2 | |
TD:< 143℃ TD:< 143℃ |
1/℃ | ISO 11359-2 | |
TD:> 143℃ TD:> 143℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity Thermal conductivity |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
ISO 868 | ||
拉伸模量 Tensile Modulus Tensile Modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-2 | ||
断裂 brk,23℃ Broken BRK, 23 ℃ |
MPa | ISO 527-2 | |
断裂 brk,125℃ Broken BRK, 125 ℃ |
MPa | ISO 527-2 | |
断裂 brk,175℃ Broken BRK, 175 ℃ |
MPa | ISO 527-2 | |
断裂 brk,275℃ Broken BRK, 275 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,23℃ Broken BRK, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
125℃ 125℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
275℃ 275℃ |
MPa | ISO 178 | |
压缩强度 Compressive Strength Compressive Strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
200℃ 200℃ |
MPa | ISO 604 | |
250℃ 250℃ |
MPa | ISO 604 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 spiral flow length Spiral flow length |
内部方法 | ||
-- -- |
cm | 内部方法 | |
-- -- |
cm | 内部方法 | |
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
表观粘度 Apparent viscosity Apparent viscosity |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 模具温度: 374°F, 熔体温度: 770°F |
4 1 mm |
5 3 mm |
6 410°C nozzle, 190°C tool |
7 Onset |
8 Midpoint |
9 Average |
10 Along flow |
11 1V |
【新闻资讯】查看全部
水性聚氨酯最具影响力
2018-07-10 日前在北京中关村示范区召开的中科院-中关村科技成果转化工作推进会上,中科院过程工程所两项成果转化项目获奖。其中,高性能绿色水性聚氨酯关键技术及产业化项目团队获得最具影响力奖。 绿色水性聚氨酯项目团队将新材料研究与节能减排需求相结合,在绿色水性聚合物及功能应用方面取得技术突破,形成系列核心技术与知识产权,并在多项VOCs减排典型领域取得重大应用进展。2016年,该团队在国家重点专项支持下研发的水性石油套管防腐防锈涂料已为天津钢管集团累计供货500余吨。2017年,该团队为中车 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |