牌号简介 About |
---|
Baydul- 660 IBS是一种用于反应注射成型(RIM)工艺的黑色、硬质聚氨酯结构泡沫体系。该系统包括一个专门设计的交互式吹扫系统(IBS),作为两个反应性液体成分提供。A组分是一种聚合物二苯基甲烷二异氰酸酯(PMDI),B组分是一种不含CFC-或HCFC发泡添加剂的配方多元醇体系。注意:由于可能存在颜料沉淀,在将桶中的内容物输送到日计量箱之前,应彻底搅动成分B。Baydur 660 IBS系统是为通用应用而设计的,用于工业和娱乐市场。这些应用通常利用了材料的强度、优异的表面光洁度和大零件性能。与任何产品一样,在给定应用中使用Baydur 660 IBS系统必须由用户提前进行测试(包括现场测试等),以确定适用性。 Baydur 660 IBS is a black-pigmented, rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Compo- nent B is a formulated polyol system containing no CFC- or HCFC-blowing additives. Note: Component B should be agitated thoroughly prior to delivery of contents of the drum to the day tank due to possible pigment settling. The Baydur 660 IBS system was designed for general-purpose applications and is used in industrial and recreational markets. The applications typically take advantage of the material's strength, excellent surface finish, and large part capability. As with any product, use of the Baydur 660 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.319 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:6.35 mm MD:6.35 mm |
0.30 到 0.50 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 2 |
5.3 | kJ/m² | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D,6.35 mm Shaw D, 6.35 mm |
37 | ASTM D2240 | |
邵氏 D,12.70 mm Shore D, 12.70 mm |
39 | ASTM D2240 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
MPa | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
压缩强度 compressive strength |
ASTM D695 | ||
6.35 mm 6.35 mm |
MPa | ASTM D695 | |
12.7 mm 12.7 mm |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.35 mm 0.45 MPa, unannealed, 6.35 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,12.7 mm 0.45 MPa, unannealed, 12.7 mm |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.5 |
【新闻资讯】查看全部
2015全球化工50强榜单新颖出炉 巴斯夫雄踞榜首
2016-08-02 美国化学会旗下《化学与工程新闻》杂志近日发布“2015年全球化工50强排行榜”。该榜单按照相关公司上年度的化学品销售额进行排名,巴斯夫以637亿美元第十次雄踞榜首,陶氏化学以488亿美元稳居第二,中石化以438亿美元位列第三。 销售额下挫盈利大增 2015年全球化工50强的合并销售收入为7752亿美元,比2014年大幅下降10.8%,主要是因为受油价大幅下跌的影响,化学品销售价格出现下降,从而导致销售收入也大幅下滑。虽然50强化工公司的销售收入出现大幅下滑, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |