牌号简介 About |
---|
Celanex® 7716是一种35%玻璃/矿物增强、无渗出、阻燃的聚对苯二甲酸丁二醇酯,具有良好的机械性能和加工性能平衡。Celanex® 7716非常适合需要抗翘曲或非常平整表面的电气应用。 Celanex 7716 is a 35% glass/mineral reinforced, non exuding, flame retarded polybutylene terephthalate which has and excellent balance of mechanical properties and processability. Celanex 7716 is well suited for electrical applications where warp resistance or very flat surfaces are required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.69 | g/cm³ | ASTM D792 |
密度 Density |
1.69 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
MD MD |
0.20 to 0.50 | % | ASTM D955 |
TD TD |
0.60 to 0.80 | % | ISO 294-4 |
MD MD |
0.25 to 0.45 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1A/5 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature 2 |
℃ | ISO 11357-2 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength 3 |
kV/mm | ASTM D149 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.90 mm 0.90 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
3 方法A(短时间) |
【新闻资讯】查看全部
巴斯夫将在湛江一体化基地建设新戊二醇装置
2022-10-13 扫描上图二维码,可以免费下载 搜料 APP 2022年10月11日巴斯夫计划在中国的湛江一体化基地投资新建一座世界级规模的新戊二醇(NPG)装置,年产量达8万公吨。新装置预计于2025年第四季 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |