牌号简介 About |
---|
Dowlex 2062GC聚乙烯树脂是一种乙烯1-辛烯共聚物,适用于铸膜应用,也是高填充化合物的优良载体树脂。它提供了优越的刚度,结合优良的耐穿刺性和光学性能,使其成为一种完美设计的树脂,以满足转换器向下测量的需要。主要特点:最佳挤出机产量和加工能力,纯或混炼,机械性能优良平衡符合:欧盟,2011年10月,美国FDA 21 CFR 177.1520(c)3.2A。详细信息请参考法规。 Dowlex™ 2062GC Polyethylene Resin is an ethylene 1-octene copolymer, suitable for cast film applications as well as excellent carrier resin for highly filled compounds. It offers superior stiffness in combination with excellent puncture resistance and optical properties, making it to a resin perfectly designed to meet converters down gauging needs. Main Characteristics: Optimum extruder output and process ability, pure or in blends Excellent balance of mechanical properties Complies with: EU, No 10/2011 U.S. FDA 21 CFR 177.1520(c)3.2a Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.939 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.8 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
膜耐刺穿性 Membrane puncture resistance |
|||
20 µm 20 µm |
6.30 | J/cm³ | ASTM D5748 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
37.0 | MPa | ASTM D882 |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
MD,20 µm MD,20 µm 2 |
MPa | ASTM D882 | |
TD,20 µm TD,20 µm 2 |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ASTM D1922 | ||
MD:20 µm MD:20 µm |
g | ASTM D1922 | |
TD:20 µm TD:20 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm 45°,20 µm |
ASTM D2457 | ||
雾度 Haze |
|||
20 µm 20 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 @ 5% Elongation |
3 Method B |
【新闻资讯】查看全部
总投资113亿!镇海炼化拟建丙烯腈、苯酚/丙酮等!打造丙烯下游产业链
2022-05-31 5月30日,中石化宁波镇海炼化有限公司高端合成新材料项目进行环评受理公示。 该项目总投资113.32亿元,选址位于宁波石化经济技术开发区中部、甬舟高速北侧区域, 项目依托镇海炼 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |