牌号简介 About |
---|
Celanex 3216是一种非渗出型(UL和CSA批准的1/32英寸V-0和1/8英寸V-5),15%玻璃纤维增强聚对苯二甲酸丁二醇酯,具有良好的机械性能和加工性能平衡。它非常适用于电气连接器应用,在这种应用中,其经UL批准的50%再研磨使用能力允许最大限度地使用购买的产品。 Sindustris ABS LTR663 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LTR663 are: Flame Rated Chemical Resistant Clarity Impact Resistant Typical applications include: Business/Office Goods Electrical/Electronic Applications Printing Applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
220℃,10.0kg 220℃,10.0kg |
12 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.40 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃,3.2mm -30℃,3.2mm |
98 | J/m | ASTM D256 |
-30℃,6.4mm -30℃,6.4mm |
98 | J/m | ASTM D256 |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
铅笔硬度 Pencil hardness |
ASTM D3363 | ||
拉伸模量 Tensile modulus 2 |
|||
3.20 mm 3.20 mm 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm Yield, 3.20 mm 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
ASTM D638 | ||
屈服,3.20 mm Yield, 3.20 mm |
% | ASTM D638 | |
断裂,3.20 mm Fracture, 3.20 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
3.20 mm 3.20 mm 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
3.20 mm 3.20 mm 4 |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
万华宁波高性能材料研究院竣工
2021-09-05 搜料网资讯: 8月29日,万华宁波高性能材料研究院举行竣工仪式。 万华化学材料解决方案事业部总经理、万华宁波高性能材料研究院院长陈连清表示,研究院将聚焦新能源汽车、智能家 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |