Tufel II 94305橡胶化合物94205和94305是20和30硬度计,低挥发性,快速固化,添加固化硅弹性体用于成型。它们可以单独使用,也可以与中间硬度计混合使用。应用包括需要短周期时间的预制成型、深断面固化以及对可提取性要求低的零件。主要特点和优点:低压碱最大限度地减少后固化时间,完全无过氧化物固化系统显著减少成型周期系统,降低成型温度范围(150-166C)(300-330F),优越的混合货架寿命,紧密表面固化,无开花半透明 Tufel II 94305 Rubber Compounds 94205 and 94305 are 20 and 30 durometer low volatile, fast-cure, addition cured silicone elastomers for molding. They may be used by themselves or blended to intermediate durometers. Applications include fabricated molding that require short cycle time, deep section cures, and parts with low extractable requirements. Key Features and Benefits LV Bases Minimize Post Cure Times Totally Peroxide-Free Cure System Significant Reduction in Molding Cycle Systems Lower Molding Temperature Range (150-166C) (300-330F) Superior Mixed Shelf Life Tight Surface Cure Non-blooming Translucency |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
22 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
8.30 | MPa | ASTM D412 |
100% 应变 100% strain |
0.400 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
1000 | % | ASTM D412 |
撕裂强度 tear strength 2 |
22.0 | kN/m | ASTM D624 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 模具 |
【新闻资讯】查看全部
巴斯夫与美克合资聚四氢呋喃装置在新疆投产
2016-07-07 7月6日,巴斯夫与新疆美克化工股份有限公司合资兴建的聚四氢呋喃新生产装置在新疆维吾尔自治区库尔勒市正式投产,开始为国内客户提供产品。 新装置年产能 5万吨,由巴斯夫与美克的合资企业巴斯夫美克化工制造(新疆)有限责任公司负责运营。 2016 年1 月,巴斯夫与美克的BDO(1,4 丁二醇)装置在库尔勒基地建成投产。该装置年产能为 10 万吨,由美克与巴斯夫的另一家合资企业美克美欧化学品(新疆)有限责任公司负责运营。这两套装置是巴斯夫第一次携手中国民营资本在新疆 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |