牌号简介 About |
---|
优异的抗应力、抗裂性和刚度、高冲击强度、中等膨胀、高熔体强度符合:美国FDA 21 CFR 177.1520(c)3.2A加拿大HPFB无异议(有限制)欧盟,2011年10月,请参考相关法规了解完整细节。UNIVAL™ DMDA-6220 NT 7高密度聚乙烯(HDPE)树脂是一种含有多用途聚合物的抗静电剂,设计用于高速生产吹塑容器,用于包装家用工业化学品(如洗涤剂、漂白剂、织物柔软剂)、洗漱用品和化妆品(如洗发水、面霜、洗剂等)、保健和医疗辅助设备,以及D食品。此外,它可以吹塑成其他薄壁零件和家居用品,也可以挤压成型材。 Excellent stress crack resistance and rigidity High impact strength Moderate swell High melt strength Complies with: U.S. FDA 21 CFR 177.1520 (c) 3.2a Canadian HPFB No Objection (with limitations) EU, No 10/2011 Consult the regulations for complete details. UNIVAL™ DMDA-6220 NT 7 High Density Polyethylene (HDPE) Resin is an antistat containing, multipurpose polymer designed for the high speed production of blow molded containers used to package household industrial chemicals (e.g., detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.), health and medicinal aids, and food products. In addition, it can be blow molded into other thin walled parts and houseware items, and also can be extruded into profiles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.953 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.38 | g/10min | |
190℃,21.6kg 190℃,21.6kg |
33 | g/10min | |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,100%非离子表面活性剂,F50 50 ℃, 100% non-ionic surfactant, F50 |
60.0 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength 2 |
168 | kJ/m² | ASTM D1822 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
|||
正割 Secant |
MPa | ASTM D790-B |
备注 |
---|
1 With limitations |
2 一般属性:这些不能被视为规格。 |
3 类型 S |
【新闻资讯】查看全部
南韩研发新型塑料薄膜 可运用于可折叠手机
2017-06-05 有“南韩麻省理工学院”之称的KAIST,研发出新型塑料薄膜,和玻璃一样硬、又和塑料一样有弹性,预料会加快可折叠手机的问世速度,最快2018年就能上市。智能手机屏幕上覆有玻璃基板,以保护屏幕免受外来冲击,而且玻璃透明无色,不会影响显示器的颜色呈现。问题是玻璃基板无法弯折、容易碎裂,不适用于可折迭式智能手机。 业界为了发展可折叠手机,用透明塑料薄膜取代玻璃基板,但是塑料薄膜虽然能够弯折,却硬度不够,无法为屏幕提供足够保护。KAIST新材料工程系教授BaeByeong-soo宣布 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |