牌号简介 About |
---|
Lupoy PC 1303AH-18有色聚碳酸酯树脂是为汽车前照灯注塑而设计的。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。主要特点紫外线稳定剂低粘度良好的模具释放列举在美国汽车制造商协会户外应用汽车前照灯上。 LUPOY PC 1303AH-18 Tint Polycarbonate Resin is designed for injection molding of auto-headlamps. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. Main Characteristics UV stabilizer Low viscosity Good mold release Listed on AMECA Applications Outdoor applications Automotive headlamps |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
18 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.15 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
|||
23℃,3.2mm 23℃,3.2mm 3 |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ASTM D256 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 4 |
|||
23℃,3.18 mm,Total Energy 23℃,3.18 mm,Total Energy 4 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ||
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
球压温度 Ball pressure temperature |
℃ | IEC 60598-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm 2.00 mm |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
2 mm,5.0 sec 2 mm,5.0 sec |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
|||
R 级 R-level |
|||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ 2 |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
2、50 mm/min |
3、0.25 mm 缺口深度 |
4、3.39 m/sec |
5、速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
挤出模具的知识,都在这里了!
2016-12-14 操作人员必须熟悉自己所操作的挤出机,要正确掌握螺杆的特性、加热和冷却的控制、仪表特性、牵引机的控制模具的结构及装配情况等,以便正确地掌握挤出工艺条件,正确地操作机器。 挤出模的调试< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |