| 牌号简介 About |
|---|
| 尼龙是第一种工程树脂。它已被应用于从电子、海洋和汽车工业到用于制造地毯的纤维。尼龙具有优异的耐磨性和低摩擦性能。它具有很好的温度、化学和冲击性能。然而，尼龙的一个缺点是容易吸收水分，因此尺寸稳定性差。Tecamid具有优良的性能平衡，使其成为汽车零件、工业阀门、铁路连接绝缘体和其他工业用途（其设计要求包括高强度、韧性和重量减轻）中金属替换的理想材料。6/6型通用标准级尼龙。天然和黑色挤压。（也可定制耐候黑色等级。） Nylon was the first engineering resin. It has been used in applications ranging from electronic, marine, and automotive industries to fibers used to make carpet. Nylon has outstanding wear resistance and low frictional properties. It has very good temperature, chemical, and impact properties. However, nylon's one weakness is a propensity to absorb moisture and thus have poor dimensional stability. TECAMID® has an excellent balance of properties which make it an ideal material for metal replacement in applications such as automotive parts, industrial valves, railway tie insulators, and other industry uses whose design requirements include high strength, toughness, and weight reduction. TECAMID™ 6/6 Type 6/6 general purpose standard grade nylon. Extruded in natural and black. (Weather Resistant Black Grade is also available as a custom.) TECAMID™ 6/12 Type 6/12 nylon. This nylon has lower moisture absorpton rates than nylon 6/6, hence superior dimensional stability. TECAMID™ ST Type 6/6 nylon. Super Tough nylon. Increased impact resistance and toughness over Tecamid™ 6/6. TECAMID™ HS Type 6/6 nylon. Heat Stabilized nylon. Increased ability to withstand the negative effects of heat exposure and increased overall service temperature over Tecamid™ 6/6. |
产品描述 Product Description
用途：阀门/阀门部件;汽车领域的应用;工业应用;通用;金属取代;
颜色：自然色,黑色
性能特点： 耐磨; 机械强度好; 耐化学性; 防火阻燃等级V-2; 冲击性能好; 低摩擦系数; 韧性好; Good Rigidity,Good flexibility,High impact resistance,Low coefficient of friction,Good wear resistance,Solvent resistance,V-2
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.14 | g/cm³ | ASTM D792 |
|
吸水率 Water absorption rate |
ASTM D570 | ||
|
23℃，24hr 23℃，24hr |
1.2 | % | ASTM D570 |
|
饱和，23℃ Saturation, 23 ℃ |
8.5 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
59 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
235 | ℃ | ASTM D648 |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
熔融温度 Melting temperature |
℃ | ASTM D2133 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ASTM D696 | |
|
比热 specific heat |
J/kg/℃ | ||
|
最高使用温度 Maximum operating temperature |
|||
|
Intermittent Intermittent |
℃ | ||
|
长期 long-term |
℃ | UL 746B | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant 4 |
ASTM D150 | ||
|
23 ℃，60 Hz 23 ℃，60 Hz |
ASTM D150 | ||
|
23 ℃，1 MHz 23 ℃，1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
23℃，60 Hz 23℃，60 Hz |
ASTM D150 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
3.00 mm 3.00 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
摩擦系数 friction coefficient 2 |
|||
|
与自身 - 动态 With oneself - dynamic 2 |
ASTM D1894 | ||
|
磨损因数 Wear factor 3 |
|||
|
0.28 MPa，0.25 m/sec 0.28 MPa，0.25 m/sec 3 |
10^-8 mm³/N·m | ASTM D3702 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 40 psi, 50 fpm |
| 3 Against Steel |
| 4 50% RH |
|
【新闻资讯】查看全部 
巴陵石化“双重点”项目建设持续推进
2022-09-26 扫描上图二维码，可以免费下载 搜料 APP 截至9月22日，巴陵石化公司己内酰胺搬迁项目已完成项目进度的73%，主体工程土建工程已基本完成。预计主体装置将于2022年底完工，项目将于 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |