牌号简介 About |
---|
LLHG-1522A是一种经认证的优质乙烯-己烯共聚物高分子量,专门为土工膜挤出应用而开发,需要最佳的ESCR平衡、韧性和良好的柔韧性。LLHG-1522A具有很好的加工性能、较宽的熔接范围、优异的熔接强度,以及改进的输出和纹理外观表面。LLHG-1522A主要应用包括填埋场覆盖层和覆盖层、用于高密度聚乙烯的共挤覆盖层、管状和平板模具项目、与高密度聚乙烯的混合物以及作为母料化合物的载体树脂。LLHG-1522A不含滑动或防阻塞物,符合FDA法规21CFR 177.1520(c)3.2(a)和大多数与食品接触使用聚乙烯的国际法规。 LLHG-1522A is a certified prime grade Ethylene-Hexene Copolymer High Molecular Weight specially developed for Geomembrane extrusion applications requiring outstanding balance of optimal ESCR, Toughness, and excellent Flexibility. LLHG-1522A offers very good processability, broad fusion range, excellent melt strength, and improved output and texture appearance surface. LLHG-1522A major applications include landfill covers and caps, coextruded cap layers for HDPE, tubular and flat die projects, blends with HDPE, and as carrier resin for Masterbatch compounds. LLHG-1522A contains no slip or antiblock, and complies with FDA regulation 21CFR 177.1520 (c) 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.14 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
15 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
> 1500 | hr | ASTM D1693 |
50 ℃,1.75 mm,10%非离子表面活性剂,F50 50 ℃, 1.75 mm, 10% non-ionic surfactant, F50 2 |
> 1500 | hr | ASTM D1693B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 4 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
1% 正割 1% secant 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3417 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Notched bent strip |
3 2.0 in/min |
4 0.051 in/min |
【新闻资讯】查看全部
日本住友化学新建PMMA回收试验工厂
2021-08-28 搜料网资讯: 据新加坡8月23日消息,日本住友化学周一表示,公司正在日本爱媛县新居滨市新建一个用于聚甲基丙烯酸甲酯(PMMA)化学回收的试点设施。 该公司在一份声明中表示,新设施 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |