牌号简介 About |
---|
Ultem 2400树脂,40%玻璃纤维填充,标准流动聚醚酰亚胺(TG 217C)。符合ECO标准,UL94 V0和5VA清单。认可颜色的Wras认证。Ultem 2400树脂,40%玻璃纤维填充,标准流动聚醚酰亚胺(TG 217C)。树脂符合RoHS标准。UL94 V0和5VA列表。 40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. WRAS certification in recognized colors. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.61 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
337℃,6.60kg 337℃,6.60kg |
4.2 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.10 to 0.30 | % | 内部方法 |
吸水率 Water absorption rate |
|||
平衡,23℃ Equilibrium, 23 ℃ |
0.90 | % | ASTM D570 |
24hr 24hr |
0.13 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-20~150℃ MD:-20~150℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
ASTM D150 | ||
耐电弧性 Arc resistance 6 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.25 mm 0.25 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
NBS烟雾密度 NBS smoke density |
|||
Flaming,Ds,4 min Flaming,Ds,4 min |
ASTM E662 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 4 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
100 mm跨距 100 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
断裂,100 mm跨度 Fracture, 100 mm span 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.2mm 3.2mm |
J/m | ASTM D256 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 0,20 in/min |
4 类型 1, 0,20 in/min |
5 0,10 in/min |
6 0,079 in/min |
7 Break |
8 80*10*4 sp=62mm |
9 80*10*4 |
10 120*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
12 钨电极 |
【新闻资讯】查看全部 ![]()
塑料添加剂和色母粒行业持续创新
2016-11-29 从今年的K2016展来看,塑料添加剂和色母粒行业的产品创新继续进行,虽然该行业面临不少挑战,包括政治和经济因素,产品价格也随着各国和国际标准的变化而走低。 普立万在K展上展示了Impress品牌的超亮金属 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |