牌号简介 About |
---|
对于高性能薄膜应用,符合美国FDA 21 CFR 177.1520(c)3.2A的要求。有关完整的详细信息,请参考法规。ELITE™ 5101G增强聚乙烯树脂是由陶氏塑料通过Init技术生产的共聚物。它具有极高的抗冲击性,结合良好的撕裂和拉伸性能。此外,对于自动化包装应用,该树脂表现出比LLDPE更高的热粘强度。 For high performance film applications Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a. Consult the regulations for complete details. ELITE™ 5101G Enhanced Polyethylene Resin is a copolymer produced via INSIT™ Technology from Dow Plastics. It offers extremely high impact resistance, combined with good tear and tensile properties. In addition, this resin exhibits higher hot tack strength than LLDPE for automated packaging applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.85 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
膜刺穿强度 Membrane puncture strength |
|||
51 µm 51 µm |
4.29 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
|||
51 µm 51 µm |
71.2 | N | 内部方法 |
膜耐刺穿性 Membrane puncture resistance |
|||
51 µm 51 µm |
J/cm³ | 内部方法 | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
MPa | ASTM D882 | |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 2 |
|||
51 µm 51 µm 2 |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 实现 2 磅/英寸 (8.8 N/25.4 mm) 热封强度的温度。 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10 英寸/分(250 mm/秒)。 |
【新闻资讯】查看全部
快递企业扎堆上调派费 真能结束多年价格战?
2021-08-31 搜料网资讯: 各家快递企业持续多年的价格战或许快要休战了。包括中通、圆通、韵达、申通、百世和极兔速递在内的加盟制快递企业,均将于9月1日起上调0.1元的派费,涨价理由为保 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |