| 牌号简介 About |
|---|
| ADIPRENE LF 1800A是一种游离TDI含量很低的TDI端接聚酯预聚物。这种预聚物的粘度也很低，可以在较低的温度下进行加工，以获得更好的热稳定性和更长的使用寿命。当用4，4’-亚甲基双（邻氯苯胺），通常称为MBCA固化时，它会产生一种高性能，80邵尔A硬度的弹性体。ADIPRENE LF 1800A的特点包括：低游离TDI含量、低粘度、长寿命、高撕裂度和拉伸强度 ADIPRENE® LF 1800A is a TDI-terminated polyester prepolymer having very low free TDI content. This prepolymer also has low viscosity, which allows it to be processed at reduced temperature for better heat stability and longer pot life. It yields a high performance, 80 Shore A hardness elastomer when cured with 4,4'-methylene-bis-(o-chloroaniline), commonly called MBCA. Features of ADIPRENE LF 1800A include: Low Free TDI Content Low Viscosity Long Pot Life High Tear and Tensile Strength |
产品描述 Product Description
用途：车轮;
加工条件：浇铸 casting
性能特点： 拉伸性能好; 耐磨; 机械强度好-撕裂; 低粘度; Low Viscosity,Good Tensile Strength,Good tear strength,Good wear resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.25 | g/cm³ | ASTM D792 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
裤型撕裂耐性 Pant tear resistance |
43.8 | N/mm | ASTM D1938 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
100% 应变 100% strain |
4.83 | MPa | ASTM D412 |
|
200% 应变 200% strain |
6.21 | MPa | ASTM D412 |
|
300% 应变 300% strain |
9.65 | MPa | ASTM D412 |
|
拉伸强度 tensile strength |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D412 | |
|
撕裂强度 tear strength |
|||
|
-- -- 2 |
kN/m | ASTM D624 | |
|
开裂 cracking |
kN/m | ASTM D470 | |
|
压缩形变 Compression deformation |
|||
|
70℃，22 hr 70℃，22 hr |
% | ASTM D395B | |
|
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
储存稳定性 storage stability |
min | ||
|
脱模时间 stripping time |
min | ||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
固化时间 Curing time |
|||
|
100℃ 100℃ |
hr | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
ASTM D2240 | ||
|
压缩强度 compressive strength |
ASTM D695 | ||
|
5% 应变 5% strain |
MPa | ASTM D695 | |
|
10% 应变 10% strain |
MPa | ASTM D695 | |
|
15% 应变 15% strain |
MPa | ASTM D695 | |
|
20% 应变 20% strain |
MPa | ASTM D695 | |
|
25% 应变 25% strain |
MPa | ASTM D695 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具 |
|
【新闻资讯】查看全部
斯道拉恩索北海工厂聚乙烯淋膜消费线投产
2018-01-29 斯道拉恩索北海工厂聚乙烯淋膜生产线日前正式投产。这是继2016年斯道拉恩索包装纸板机和漂白化学热磨机械浆(BCTMP)生产线投产后，斯道拉恩索集团在中国的又一重大投资投入运营。 斯道拉恩索北海工厂聚乙烯淋膜生产线于2016年10月动工建设，取得了零损失工时事故记录的卓越安全绩效。生产线采用了行业最先进的设备及技术，并执行最高卫生标准，确保产品安全。工厂运营团队年轻而富有活力，拥有在斯道拉恩索欧洲工厂培训的丰富经验，践行世界级制造的管理理念。 该聚乙烯淋膜生产 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付