牌号简介 About |
---|
Eltex® PF6612KJ是一种产于欧洲的茂金属LLDPE级。优点和特点Eltex® PF6612KJ是一种含有己烯-1作为共聚单体的聚乙烯共聚物,由茂金属催化剂制备。它具有以下特性:高冲击强度和刚性优良的光学特性非常好的气泡稳定性和可挤压性低温密封特性Eltex® PF6612KJ具有高滑动膜和易开启特性。添加其他聚合物、母粒和颜料可能会改变膜滑性和防堵塞性能,已开发出Eltex® PF6612KJ用于整理收缩膜、食品包装和其他薄膜应用,在这些应用中,需要膜强度和刚度之间的良好平衡以及良好的光学性能。此外,Eltex® PF6612KJ提供了容易挤压。 Eltex® PF6612KJ is a metallocene LLDPE grade produced in Europe. Benefits & Features Eltex® PF6612KJ is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties: High impact strength and rigidity Excellent optical properties Very good bubble stability and extrudability Low temperature sealing characteristics Eltex® PF6612KJ offers high slip film with easy opening properties. Addition of other polymers, masterbatch and pigments may alter film slip and antiblock performance Applications Eltex® PF6612KJ has been developed for use in collation shrinkwrap, food packaging and other thin film applications where an excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex® PF6612KJ offers easy extrudability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.927 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.3 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
< 0.30 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
230 | MPa | ISO 527-3 |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature 3 |
℃ | ASTM D3418 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 Silica |
2 一般属性:这些不能被视为规格。 |
3 2nd heating |
【新闻资讯】查看全部
丙烯:全球扩能引发剧烈竞争
2016-03-09 全球乙烯裂解原料轻质化的趋势以及原油价格高企等因素,促进了近几年丙烯新兴生产工艺的兴起和快速发展,丰富了丙烯的来源。但随着全球油价的大幅下滑,新兴生产工艺成本压力加大,不同工艺的竞争更加激烈。 IHS公司分析认为,短期内丙烯产能增长仍然明显快于需求增长,给全球丙烯价格带来压力。2017年之后,全球产能增长会有所放缓,但市场仍然需要时间消化近几年快速增加的产能。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |