| 牌号简介 About |
|---|
| 拉努芬LLF 182N是一种线性低密度通用吹塑薄膜挤出聚乙烯，具有较高的机械性能和良好的加工性能。拉努芬LLF 182N既不含助滑剂，也不含防堵剂。由该树脂制成的薄膜具有良好的韧性、高拉伸性能和优异的抗穿刺性能。拉努芬LLF 182N是一种特别适合与低密度聚乙烯和/或高密度聚乙烯混合，共挤，重型袋和拉伸薄膜应用。 LANUFENE LLF 182N is a linear low density polyethylene for general purpose blown film extrusion with high mechanical properties and good process-ability. LANUFENE LLF 182N contains neither slip additive nor anti-blocking agent. The film produced from this resin characteristically exhibits good toughness, high tensile properties, and outstanding puncture resistance. LANUFENE LLF 182N is a particularly suitable for blending with LDPE and/or HDPE, Coextrusion, heavy duty bags and stretch film application. |
产品描述 Product Description
用途：重包装袋;薄膜;拉伸缠绕;混合;
加工条件：薄膜挤出 Film extrusion
性能特点： 拉伸性能好; 食品接触; 韧性好; 抗穿孔性; 易加工; Excellent Processability,Good flexibility,Food contact compliance,Good Tensile Strength,Puncture Resistant
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，21.6kg 190℃，21.6kg |
2.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
38 | µm | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD：38 µm 1% secant, MD: 38 µ m |
220 | MPa | ASTM D882 |
|
1% 正割，TD：38 µm 1% secant, TD: 38 µ m |
260 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
极限 limit |
MPa | ASTM D638 | |
|
MD，断裂，38 µm MD, fracture, 38 µ m |
MPa | ASTM D882 | |
|
TD，断裂，38 µm TD, fracture, 38 µ m |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
断裂 fracture |
% | ASTM D638 | |
|
MD，断裂，38 µm MD, fracture, 38 µ m |
% | ASTM D882 | |
|
TD，断裂，38 µm TD, fracture, 38 µ m |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
|||
|
38 µm 38 µm |
g | ASTM D1709-A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，38 µm 45°，38 µm |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
38 µm 38 µm |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
日本住友化学在中国增强PP复合资料及TPE生产销售
2017-05-24 日本住友化学5月23日宣布已于四川成都新设PP复合材料的生产及销售据点----成都东承住化汽车复合塑料有限公司(2016年10月注册)，同时将在辽宁大连工厂投资设备生产热塑性弹性体TPE。 PP复合材料在PP(聚丙烯)基础上添加了合成橡胶、玻璃纤维、无机填料等，具有高刚性、高抗冲性，主要用于汽车保险杠及内饰材料。住友化学公司认为中国拥有世界上规模最大的汽车市场，汽车行业对PP复合材料的需求也不断扩大，且成都是中国新一线城市，经济保持高速发展，在此设立PP复合材料生产及销售基 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付