| 牌号简介 About |
|---|
| cycoloy cy6414树脂阻燃改性PC混合物，采用无溴和无氯阻燃系统，为家电、照明和电气市场提供高热。cycoloy cy6414树脂阻燃改性PC采用无溴和无氯阻燃系统，为app提供高热。在电器、照明和电气市场的应用。 CYCOLOY CY6414 impact modified Polycarbonate(PC) resin is a high heat grade that can be injection molded. This non-chlorinated, non-brominated flame retardant impact modified PC has a UL V0 & 5VB flame rating. CYCOLOY CY6414 resin is an excellent candidate for a wide variety of applications including appliances, lighting and electrical. |
产品描述 Product Description
用途：电气/电子应用领域;照明应用;电器用具;
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 耐高温; 防火阻燃等级5VB; 阻燃; Halogen free,Flame Characteristics,High Heat Resistance,V-0,5VB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.18 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
260℃，5.0kg 260℃，5.0kg |
14 | g/10min | ASTM D1238 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
2330 | MPa | ASTM D638 |
|
拉伸强度 tensile strength 3 |
|||
|
断裂 fracture 3 |
62.0 | MPa | ASTM D638 |
|
屈服 yield 3 |
64.0 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 4 |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
0℃ 0℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
0℃ 0℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
IEC 60695-10-2 | ||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
125℃ 125℃ 5 |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
1 kHz 1 kHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
1 kHz 1 kHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.20 mm 1.20 mm |
UL 94 | ||
|
2.50 mm 2.50 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index 5 |
|||
|
0.75 mm 0.75 mm 5 |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire 5 |
IEC 60695-2-13 | ||
|
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
|
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.20 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.079 in/min |
| 5 Yield |
| 6 80*10*3 sp=62mm |
| 7 80*10*4 sp=62mm |
| 8 80*10*4 |
| 9 80*10*4 mm |
| 10 by VDE |
|
【新闻资讯】查看全部 
浦项制铁化工在韩建电池材料厂
2022-03-20 近日，浦项制铁化工宣布，该公司将投资6000亿韩元(约合4.93亿美元)在韩国光阳的Sepoong工业园区建设一座产能10万吨/年的正极材料前体工厂。 该公司表示，10万吨/年产能可满足制造120万 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付