牌号简介 About |
---|
Kalix® 5950 HFFR是一种无卤阻燃剂(ul-94v0,0.4 mm),高度增强的聚酰胺材料,专门为高强度和刚度应用而设计,要求具有良好的抗冲击性和成型后的尺寸稳定性。该公式还解决了与玻璃纤维增强材料的各向异性收缩有关的翘曲问题,以便更容易实现精密公差成型。它的低粘度和优良的流动性能使这种材料非常适合于填充具有薄壁截面的部件,如移动电子工业中遇到的部件。黑色:Kalix 5950 BK 000 HFFR白色:Kalix 5950 WH 000 HFFR Kalix® 5950 HFFR is a halogen-free, flame retardant (UL-94 V0 at 0.4 mm), highly reinforced polyamide material specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry. Black: Kalix® 5950 BK 000 HFFR White: Kalix® 5950 WH 000 HFFR |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.68 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate 3 |
内部方法 | ||
TD TD |
0.18 | % | 内部方法 |
MD MD |
0.060 | % | 内部方法 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.11 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
20000 | MPa | ISO 527-2 |
平衡,50% RH 50% RH,平衡 |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
断裂弯曲应变 Fracture bending strain |
% | ISO 178 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
50% RH,平衡 50% RH, balanced |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,平衡,50% RH Fracture, balanced, 50% RH |
% | ISO 527-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant 4 |
|||
2.40 GHz 2.40 GHz 4 |
ASTM D2520 | ||
耗散因数 Dissipation factor 4 |
|||
2.4 GHz 2.4 GHz 4 |
ASTM D2520 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm,所有颜色 0.40 mm, all colors |
UL 94 | ||
1.50 mm,所有颜色 1.50 mm, all colors |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 索尔维测试方法。收缩率会根据部件的设计和加工条件而改变。请接洽索尔维技术代表,获取更多信息。 |
3 方法 B |
【新闻资讯】查看全部
巴斯夫将全球光引发剂业务售予IGM Resins
2016-08-31 ・ 巴斯夫将专注于面向光固化市场的树脂和添加剂技术 ・ 继续为电子行业提供高性能光引发剂 巴斯夫已将全球光引发剂业务售予全球性的光固化材料生产和供应商荷兰IGM Resins B.V.。电子行业是巴斯夫战略性专注领域之一,因此满足该行业客户特定需求的高性能光引发剂将不属于此次剥离的范围。 光引发剂被多个行业用于光固化配方。典型的终端应用包括家具和地板涂料,以及用于印刷和包装的油墨。 “此次交易能让巴斯夫专注于面向光固化市场的树 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |