BMC 620M模塑料是一种矿物填充的玻璃纤维增强聚酯化合物,适合于压缩,填充器注射成型,具有冲击强度高、成型性好、整体电气性能和阻燃性好等特点。典型应用包括相分离器断路器外壳,以及要求军用规格MIL-M-14G MAI-60型性能的应用。虽然BMC 620M是为满足本规范而设计的,但尚未提交给QPL认可。BMC 620M模塑料是以一系列工业颜色生产的,仅以散装形式供应。 BMC 620M molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression, and stuffer injection mo lding It is characterized by high impact strength, good moldability, excellent overall electrical properties and flame resistance. Typical applications include phase separators circuit breaker housings, and applications requiring the properties of Military specification Mil-M-14G Type MAI-60. Although BMC 620M was designed to meet this specification, it has not been submitted for QPL recognition. BMC 620M molding compound is produced in a range of industrial colors, and is supplied in bulk form only. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.86 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:模压成型 MD: Compression molding |
0.15 to 0.25 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.13 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
530 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,模压成型 1.8 MPa, unannealed, molded |
260 | ℃ | ASTM D648 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
6.40 mm 6.40 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
巴氏硬度 Babbitt hardness 2 |
ASTM D2583 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
浙江自贸试验区舟山片区创下10项“全国之最 ”
2022-04-09 五年来,浙江自贸试验区舟山片区服务国家战略, 围绕建设大宗商品资源配置新高地,聚焦油气全产业链为核心的大宗商品投资贸易便利化自由化, 实现了无中生油聚气发展的改革突 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |