牌号简介 About |
---|
KM-199IB是一种高流动冲击共聚物,用于注塑成型,具有良好的加工性、刚度、冲击强度平衡。由于其高流动性,可用于大尺寸应用的注射成型,也可作为适用于汽车内外特性的聚丙烯复合材料的基础树脂:良好的流动性抑制(虎纹) KM-199IB is a high flow impact copolymer for injection molding application with excellent processability, stiffness-impact strength balance. It can be used for injection molding for large-size application due to its high flowability and as a base resin for PP composite material that is applicable to automobile exterior and interior Characteristics: Excellent processibility Suppression of flow mark (tiger stripe) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.910 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
80 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
49 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
125 | ℃ | ASTM D648 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
95 | ASTM D785 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
5月份不同来源制聚丙烯利润简析与2021年6月展望
2021-06-09 搜料网资讯: 6月各来源制 聚丙烯 盈利情况多出现不同程度的下滑,主要受制于聚 丙烯 相对弱势的价格以及原料表现则多坚挺。因动力煤的价格居高难下,因此油制聚丙烯的成本水平 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |