牌号简介 About |
---|
无卤有机填充三聚氰胺改性聚酯模塑料,低后收缩,电性能好,耐热性高,滑动性能好,在电气工程中具有很好的耐磨性,主要是断路器、继电器、开关、接触端子等电气零件。他的产品符合重金属和PCA的允许上限,也符合欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)的要求。 Halogen-free, organically and inorganically filled melamine-modified Polyester moulding compound Low post-shrinkage, very good electrical values, high heat resistance,very good sliding behaviour, very good wear stability Moulded parts in electrical engineering, mainly electrical parts such as circuit breakers, relays, switches, contact terminals This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.70 到 1.80 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.75 到 0.95 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate 1 |
|||
MD MD 1 |
0.70 到 1.0 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.80 | % | ISO 62 |
后收缩 Post contraction 2 |
0.20 到 0.40 | % | ISO 2577 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ||
注塑成型 injection molding |
MPa | ||
拉伸强度 tensile strength |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ||
注塑成型 injection molding |
MPa | ||
弯曲模量 Bending modulus |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ||
注塑成型 injection molding |
MPa | ||
弯曲强度 bending strength |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ||
注塑成型 injection molding |
MPa | ||
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
模压成型 Compression Molding |
kJ/m² | ||
注塑成型 injection molding |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
模压成型 Compression Molding |
kJ/m² | ||
注塑成型 injection molding |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~100℃ MD:50~100℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
最高使用温度 Maximum operating temperature |
IEC 60216 | ||
<50 h <50 h |
℃ | ||
20,000 h 20,000 h |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩成型压力 Compression molding pressure |
MPa | ||
压缩成型温度 Compression molding temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compression Molded |
3 168 h / 110°C |
【新闻资讯】查看全部
大庆钻探海外市场再创佳绩
2021-09-07 搜料网资讯: 8月31日,从中石油了解到,今年前7个月,大庆钻探在海外市场签约额达33.91亿元人民币,呈现出市场开发见成效、优化生产提时效、精益管理促增效的良好局面。 该公司紧 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |