牌号简介 About |
---|
Menzolit® BMC 1000是一种基于不饱和聚酯树脂的整体模塑料。该产品是玻璃纤维增强,含有矿物填料。如果发生火灾,产品不会熔化,也不会形成液滴,也不会产生过量的烟雾。这种材料是在加热的钢模中注射成型的。建议使用镀铬工具。该产品不含卤素。Menzolit® BMC 1000是一种用于抗水解应用的特殊BMC。将玻璃含量设置为能够提供足够的可塑性和高强度和刚度特性的水平。典型应用是暴露在潮湿环境中的组件。暴露在水或潮湿大气中的外壳、盖子和功能部件,如热带国家或工厂设备,是使用这种材料的典型例子。 Menzolit® BMC 1000 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® BMC 1000 is a special BMC for hydrolysis resistant applications. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. Typical applications are components which are exposed to a humid environment. Housings, covers and functional components which are exposed to water or wet atmosphere, like in tropic countries or plant equipment, are typical examples for the use of this material. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.80 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
-- -- 2 |
0.0 | % | DIN 53464 |
-- -- |
0.15 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
< 0.30 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
模压成型 Compression Molding |
13000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
模压成型 Compression Molding |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature |
℃ | 内部方法 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Glow Bar Glow Bar |
IEC 60707-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Post Molding Shrinkage |
【新闻资讯】查看全部
2025年之前,欧洲将塑料瓶的回收率从60%提高到90%
2018-05-17 据英国路透社5月15日报道,欧洲瓶装水生产商15日设定了一项目标,即到2025年之前,要将塑料瓶的回收率从60%提高到90%,以提高回收利用率和减少污染。 “欧洲瓶装水联合会”在一份声明中表示,塑料瓶包装 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |