牌号简介 About |
---|
TAISOX 6534F是一种低密度聚乙烯材料,。 该产品在北美洲、欧洲或亚太地区有供货,。 TAISOX 6534F的主要特性有: Antiblock 软件 滑动 美观 TAISOX 6534F的典型应用领域为:电影 TAISOX® 6534F is a Low Density Polyethylene material. It is available in Asia Pacific, Europe, or North America. Important attributes of TAISOX® 6534F are: Antiblock Good Aesthetics Slip Typical application of TAISOX® 6534F: Film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
5.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
30 | µm | |
薄膜厚度 film thickness |
0.6-2.4 mil (15-60 µ | ||
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:30 µm,吹塑薄膜 1% secant, MD: 30 µ m, blow molded film |
186 | MPa | ASTM D882 |
1% 正割,TD:30 µm,吹塑薄膜 1% secant, TD: 30 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,30 µm,吹塑薄膜 MD, yield, 30 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,30 µm,吹塑薄膜 TD, yield, 30 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,30 µm,吹塑薄膜 MD : Break, 1.2 mil, Blown Film |
MPa | ASTM D882 | |
TD,断裂,30 µm,吹塑薄膜 TD, fracture, 30 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,30 µm,吹塑薄膜 MD : Break, 1.2 mil, Blown Film |
% | ASTM D882 | |
TD,断裂,30 µm,吹塑薄膜 TD, fracture, 30 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
30 µm,吹塑薄膜 30 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:30 µm,吹塑薄膜 MD: 30 µ m, blow molded film |
g | ASTM D1922 | |
TD:30 µm,吹塑薄膜 TD: 30 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,30 µm,吹塑薄膜 45 °, 30 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
30 µm,吹塑薄膜 30 µ m, blow molded film |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
ASTM D1894 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美国塑料化学回收遭受“打击”
2022-03-14 化学回收一直是一个有争议的话题。 近日,美国自然资源保护委员会(NRDC)的一份研究报告称, 美国大多数塑料化学回收工厂实际上并没有回收塑料,而是将其转化成燃料,同时在低 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |