牌号简介 About |
---|
洛特利24MA005是高压自由基聚合法生产的乙烯与丙烯酸甲酯的无规共聚物。由于丙烯酸甲酯含量的原因,洛特利24MA005可用于需要柔软性、柔韧性和极性的应用。典型应用是柔性薄膜、聚酯改性和电缆化合物。 LOTRYL® 24MA005 is a random copolymer of Ethylene and Methyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the methyl acrylate content, LOTRYL® 24MA005 can be used for applications where softness, flexibility and polarity are required. Typical applications are flexible film, polyesters modification and cable compounds. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ISO 1183 , ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.40 到 0.60 | g/10min | ASTM D1238,ISO 1133 |
甲基丙烯酸含量 Methacrylic acid content |
23.0 到 26.0 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
45.0 | ℃ | ISO 306/A , ASTM D1525 2 |
熔融温度 Melting temperature |
72.0 | ℃ | ISO 11357-3 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,模压成型 Shaw A, molded |
ASTM D2240 , ISO 868 | ||
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ASTM D638 , ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ASTM D638 , ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ASTM D790 , ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
恒力石化拟建年产250万吨PTA项目
2018-04-18 恒力石化股份有限公司近日公告,下属孙公司恒力石化(大连)有限公司计划投资建设年产250万吨PTA-4项目。 项目总投资人民币约29亿元,位于大连长兴岛经济区石化产业园区内。项目预计于2018年年底完成土建,2019年四季度调试试生产。 公告称,项目毗邻恒力石化一、二期现有产能,建成后,下属孙公司恒力石化现有PTA产能将由660万吨/年增加至910万吨/年,且新建装置采用英威达最新工艺技术,有利于上市公司进一步强化在聚酯化纤产业链上游PTA行业的技术、规模与成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |