| 牌号简介 About |
|---|
| Vestolit G 138是一种乙烯基酯共聚物分散树脂，在低加工温度下表现出快速融合，从而节省能源，并能够与热敏性基板一起工作。乙烯基酯共聚物具有稳定的布鲁克菲尔德粘度老化特性。它具有机械和化学发泡性能。Vestolit G 138建议用于需要低温加工的应用，如地毯瓷砖和散铺衬垫、塑料溶胶油墨、一般低温加工应用和汽车密封剂。 VESTOLIT G 138 is a vinyl ester copolymer dispersion resin, exhibiting fast fusion at low processing temperatures, resulting in energy savings and the ability to work with heat sensitive substrates. The vinyl ester copolymers exhibit stable Brookfield Viscosity aging characteristics. It provides mechanically and chemically foamable properties. VESTOLIT G 138 is recommended for applications where low processing temperatures are required such as carpet tile and walk off mat backings, plastisol inks, general low temperature processing applications, and automotive sealants. |
产品描述 Product Description
用途：地毯背衬;汽车领域的应用;密封剂;
颜色：白色
加工条件：滚塑成型
性能特点： 快速融合; 低VOC; Fast Fusion,Low odor
| 技术参数 Technical Data | |||
|---|---|---|---|
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
最优拉伸 Optimal stretching 4 |
|||
|
FF FF 4 |
21.0 | MPa | ASTM D638 |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss 5 |
|||
|
60 Degree Fused 5 mins @ 350F 60 Degree Fused 5 mins @ 350F 5 |
89 | % | 内部方法 |
|
透光率 Transmittance 6 |
94 | % | 内部方法 |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Copolymer Content Copolymer Content 9 |
4.8 | % | 内部方法 |
|
North细度 North fineness 10 |
4.75 | Hegman | 内部方法 |
|
Residual Vinyl Chloride Monomer Residual Vinyl Chloride Monomer 11 |
ppm | 内部方法 | |
|
甲醇可萃取 Methanol extractable 12 |
% | 内部方法 | |
|
聚合过程 polymerization process |
|||
|
凝胶温度 Gel temperature 13 |
℃ | 内部方法 | |
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ASTM D792 | |
|
K-Value K-Value 1 |
内部方法 | ||
|
固有粘度 Intrinsic viscosity |
ASTM D1243-60-A | ||
|
湿度 humidity 2 |
|||
|
Karl Fisher Karl Fisher 2 |
% | 内部方法 | |
|
体积密度 bulk density |
g/l | ||
|
相对粘度 Relative viscosity 3 |
内部方法 | ||
|
布络克菲尔德粘度 Brookfield viscosity 7 |
内部方法 | ||
|
初始粘度@ 2 rpm Initial viscosity @ 2 rpm |
Pa·s | 内部方法 | |
|
初始粘度@ 2 rpm Initial viscosity @ 2 rpm |
Pa·s | 内部方法 | |
|
一天粘度@ 2 rpm One day viscosity @ 2 rpm |
Pa·s | 内部方法 | |
|
一天粘度@ 20 rpm One day viscosity @ 20 rpm |
Pa·s | 内部方法 | |
|
切断流出 Cut off the outflow 8 |
|||
|
95 psi 95 psi 8 |
g/10 min | 内部方法 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Correlation, 0.5g/100ml |
| 3 VESTOLIT STP 683 |
| 4 Correlation, Cyclohexanone 1% |
| 5 With provided formulation |
| 6 VESTOLIT ALTC 65 (with provided formulation) |
| 7 VESTOLIT ALTC 66 (with provided formulation) |
| 8 VESTOLIT ALTC 23 (with provided formulation) |
| 9 VESTOLIT ALTC 22 (with provided formulation) |
| 10 VESTOLIT STP PT-LA-026 |
| 11 VESTOLIT STP 390 (with provided formulation) |
| 12 VESTOLIT STP 1005 |
| 13 VESTOLIT ALTC 29 (with provided formulation) |
| 14 VESTOLIT STP 894 |
|
【新闻资讯】查看全部
开祥化工PBT安装运转负荷已提至100%
2018-10-29 10月24日， 河南开祥精细化工有限公司发布消息称，该公司PBT(聚对苯二甲酸丁二醇酯)装置运行负荷已提至100%，创历史最好水平。 该装置是国内单套产能最大的PBT生产装置，拥有首套国产酯化法生产技术。在装置投产初期，工艺波动、设备启停、产品不合格等问题不断。 “那个时候我们已经投入了大量的人力物力，如果选择采用国内惯用的日本或者德国技术的话，多年的努力将付诸东流，而且在不断变幻的市场面前，我们将丧失成本优势和市场先机。因此，国产化道路一定要坚持下去。”开 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付